A Probabilistic Model of the Unidirectional Tensile Strength of Fiber-Reinforced Polymers for Structural Design

Table 1

Summary of the experimental database.

Set no.	Set size	Material	Specimen size (mm)			Test speed	Standard	Reference
			tf	bf	lf
1	7	Glass/epoxy laminate	1.5	12.7	25.4	n.a.	n.a.	Rosen 1964 [14]
2	5	Glass/epoxy laminate	1.5	12.7	25.4	n.a.	n.a.	Zweben 1968 [15]
3	6	Glass/epoxy laminate	1.5	12.7	25.4	n.a.	n.a.
4	13	Carbon/epoxy laminate	n.a.	n.a.	n.a.	n.a.	n.a.	Bullock 1974 [16]
5	36	Carbon/epoxy tow	n.a.	n.a.	n.a.	n.a.	n.a.
6	29	Glass/epoxy prepreg	n.a.	25.4	203	n.a.	n.a.	Sun and Yamada 1978 [17]
7	25	Carbon/epoxy panel coupon	n.a.	12.7	229	n.a.	D3039	Whitney and Knight 1980 [18]
8	20	Carbon/epoxy panel coupon	n.a.	12.7	229	n.a.	D3039
9	36	Carbon/epoxy panel coupon	n.a.	12.7	229	n.a.	D3039
10	49	S2-glass/epoxy	n.a.	n.a.	n.a.	n.a.	n.a.	Shimokawa et al. 1989 [19]
11	30	Carbon/epoxy laminate	n.a.	38	300	n.a.	n.a.	Beyerlein and Phoenix 1990 [20]
12	31	Carbon/epoxy microlaminate	n.a.	n.a.	n.a.	n.a.	n.a.
13	21	Carbon/epoxy microlaminate	n.a.	n.a.	n.a.	n.a.	n.a.
14	48	Carbon/epoxy microlaminate	n.a.	n.a.	n.a.	n.a.	n.a.
15	24	Carbon/epoxy microlaminate	n.a.	n.a.	n.a.	n.a.	n.a.
16	30	Carbon/epoxy microlaminate	n.a.	n.a.	n.a.	n.a.	n.a.
17	6	Carbon/epoxy prepreg	3.4	38.2	324	0.00047 s^−1	D3039	Lavoie 1997 [21]
18	7	Carbon/epoxy prepreg	4.5	50.9	431	0.00047 s^−1	D3039
19	7	Carbon/epoxy prepreg	1.1	12.7	108	0.00047 s^−1	D3039
20	7	Carbon/epoxy prepreg	2.2	25.5	219	0.00047 s^−1	D3039
21	7	Carbon/epoxy prepreg	3.4	38.2	324	0.00047 s^−1	D3039
22	7	Carbon/epoxy prepreg	1.1	12.7	108	0.00047 s^−1	D3039
23	8	E-glass/epoxy laminate	1.6	100	250	3 mm/min	n.a.	Cattell and Kibble 2001 [22]
24	14	E-glass/epoxy laminate	1.0	100	250	3 mm/min	n.a.
25	20	Carbon/epoxy laminate	8.0	10	60	2.64 mm/min	D3039	Ochola 2004 [23]
26	20	Glass/epoxy laminate	8.0	10	60	2.64 mm/min	D3039
27	19	Carbon/epoxy sheet	0.89	15	206	1.33 mm/min	D3039	Birgoren and Husnu Dirikolu 2004 [24]
28	6	E-glass/epoxy	1.2	15	250	1 mm/min	ISO 527	Makarov et al. 2004 [25]
29	5	E-glass/epoxy	1.2	15	250	3.8 s^−1	n.a.
30	5	E-glass/epoxy	1.2	15	250	22.65 s^−1	n.a.	Makarov et al. 2004 [25]
31	5	E-glass/epoxy	1.2	15	250	32.34 s^−1	n.a.
32	5	E-glass/epoxy	1.2	15	250	39.85 s^−1	n.a.
33	5	E-glass/epoxy	1.2	15	250	40.89 s^−1	n.a.
34	30	E-glass/vinyl ester coupon	6.4	25.4	330	2.5 mm/min	D3039	Zureick et al. 2006 [3]
35	30	E-glass/vinyl ester coupon	9.6	25.4	330	2.5 mm/min	D3039
36	24	E-glass/vinyl ester coupon	6.4	25.4	330	2.5 mm/min	D3039
37	24	E-glass/vinyl ester coupon	6.4	25.4	330	2.5 mm/min	D3039
38	30	E-glass/vinyl ester coupon	n.a.	n.a.	n.a.	n.a.	n.a.
39	5	Glass/epoxy laminate	1.0	12.7	82.7	0.0017 s^−1	n.a.	Shokrieh and Omidi 2009 [26]
40	5	Glass/epoxy laminate	1.0	12.7	82.7	0.55 s^−1	n.a.
41	5	Glass/epoxy laminate	1.0	12.7	82.7	5.6 s^−1	n.a.
42	5	Glass/epoxy laminate	1.0	12.7	83.7	46 s^−1	n.a.
43	5	Glass/epoxy laminate	1.0	12.7	82.7	85 s^−1	n.a.
44	30	Carbon/epoxy plate	1.0	5.0	120	0.5 mm/min	n.a.	Okabe et al. 2010 [27]
45	20	Carbon/epoxy laminate	2.0	25	230	2 mm/min	GB/T3354	Wang and yang 2010 [28]
46	20	Carbon/epoxy laminate	2.0	15	175	2 mm/min	D3039	Du et al. 2012 [29]
47	7	Glass/polyester panel coupon	1.0	15	250	2 mm/min	D3039	Gohil and Shaikh 2013 [8]
48	60	Carbon/epoxy panel coupon	0.8	12.5	330	2 mm/min	D3039	Sasikumar et al. 2015 [30]
49	9	Glass/epoxy laminate	0.6	2.64	105	120 s^−1	n.a.	Ou and Zhu 2015 [13]
50	8	Glass/epoxy laminate	0.6	2.64	105	40 s^−1	n.a.
51	10	Glass/epoxy laminate	0.52	22	105	1/600 s^−1	n.a.	Ou et al. 2016 [31]
52	9	Glass/epoxy laminate	0.52	22	105	50 s^−1	n.a.
53	8	Glass/epoxy laminate	0.52	22	105	40 s^−1	n.a.
54	8	Glass/epoxy laminate	0.52	22	105	40 s^−1	n.a.
55	72	Carbon/polyamide6 laminate	1.0	25	250	1 mm/min	JISK7165	Ma et al. 2016 [32]
56	58	Carbon/epoxy laminate	1.0	25	250	1 mm/min	JISK7165
57	59	Carbon/polyamide6 laminate	1.0	15	250	1 mm/min	D3039	Ma et al. 2017 [33]
58	67	Carbon/epoxy laminate	1.0	15	250	1 mm/min	D3039