Mechanical Behavior of Q460 High-Strength Steel under Low-Cycle Fatigue Loading

Table 5

Summary of test results.

Specimen label	E (×105 MPa)	fy (MPa)	fu (MPa)	εu	ε	fy/fu	W (%)	Em (J)	n (cycles)	Failure mode
H-A-1	2.11	549	626	11.00	18.94	0.62	22.40	444	1	I
H-B-1	1.97	480	509	1.59	2.32	0.71	4.00	49	1	II
H-C-1	2.00	321	462	5.09	9.86	0.68	14.00	154	1	II
H-D-1	1.92	280	419	6.38	13.45	0.64	16.00	199	1	II
H-A-2	2.14	548	632	12.00	19.72	0.62	27.00	476	9	I
H-B-7	1.94	510	603	5.02	6.52	0.54	10.00	145	9	III
H-C-9	2.23	316	452	3.81	5.73	0.65	16.00	74	9	III
H-D-9	2.11	368	414	6.14	12.98	0.65	18.00	200	9	III
H-A-3	2.16	550	625	11.95	18.89	0.60	25.60	445	6	I
H-B-8	1.96	450	560	2.67	3.74	0.57	6.00	87	8	III
H-C-10	2.24	303	443	4.67	4.63	0.67	14.00	66	7	III
H-D-10	2.14	370	414	5.46	11.78	0.65	15.00	179	7	III
H-C-11	2.13	305	452	5.30	10.68	0.66	15.00	158	12	III
H-D-11	2.13	385	423	6.22	13.09	0.67	17.00	208	12	III
H-A-4	2.17	546	613	11.19	18.82	0.61	26.60	447	9	I
H-C-12	2.13	321	460	5.04	8.94	0.69	12.70	142	11	III
H-D-12	2.14	373	417	6.73	13.73	0.66	17.00	213	11	III
H-C-13	2.18	301	451	4.34	10.81	0.67	14.00	162	20	III
H-D-13	2.23	368	406	6.74	13.85	0.66	18.00	213	20	III
L-A-1	2.11	556	683	18.83	28.21	0.45	29.60	1226	1	I
L-B-1	2.29	479	601	1.98	3.45	0.63	7.00	174	1	II
L-C-1	2.08	382	450	5.74	10.05	0.63	16.00	306	1	II
L-D-1	2.25	426	520	7.06	14.83	0.44	22.00	606	1	II
L-A-2	2.18	515	708	8.73	16.18	0.59	24.40	939	9	I
L-B-14	1.84	350	564	2.15	2.88	0.62	6.00	143	9	III
L-C-9	2.05	315	456	6.08	11.78	0.63	14.40	353	9	III
L-D-9	1.88	350	529	6.70	13.14	0.67	18.00	525	9	III
L-A-3	2.20	551	701	8.54	17.42	0.64	24.00	954	6	I
L-B-15	1.90	316	581	1.52	2.83	0.54	7.10	124	6	III
L-C-10	2.30	329	446	6.44	12.46	0.65	14.00	354	7	III
L-D-10	2.03	363	567	5.29	11.79	0.64	17.60	505	7	III
L-A-4	2.34	543	712	8.82	19.43	0.62	26.00	1096	10	I
L-B-16	1.89	342	614	2.00	2.32	0.56	4.80	146	10	III
L-C-11	2.31	369	445	6.50	11.50	0.61	13.60	333	12	III
L-D-11	1.96	333	545	4.53	9.52	0.61	16.00	411	12	III
L-C-12	1.82	373	454	5.92	11.37	0.60	16.00	351	11	III
L-D-12	2.17	351	545	4.88	12.04	0.65	18.00	538	11	III
L-C-13	2.01	402	449	5.51	9.47	0.67	12.40	288	20	III
L-D-13	2.16	353	549	5.26	12.64	0.64	16.00	544	20	III
R-A-1	2.30	550	742	11.39	17.16	0.61	20.00	334	1	I
R-A-3	2.05	554	721	9.93	16.85	0.55	22.00	334	6	I
R-A-4	2.04	561	714	10.04	14.74	0.56	21.50	292	10	I
R-A-5	1.95	563	698	9.67	12.72	0.56	16.00	243	9	I
R-A-6	1.96	573	737	9.72	17.90	0.55	24.00	358	16	I