Evaluating the Effects of Chemical Composition on Induction Heating Ability of Fe₂O₃-CaO-SiO₂ Glass Ceramics

Table 5

Magnetic parameters of the samples.

	A1S1	A1S3	A1S5	A1S7	A1S9	A2P1	A2P7
(G)	147.76	124.82	206.83	106.24	82.45	113.85	87.87
(emu/g)	1.99	2.06	3.32	19	17.09	10.99	10.65
(emu/g)	13.27	10.30	13.28	63.33	48.83	36.63	38.04
(emu/g)	0.33	0.41	0.60	2.30	0.78	2.25	3.04
Interpolated hysteresis area	65649	176034	287151	1683193	525486	923229	980057

Note: values were normalized to the total weight of the sample; values were normalized to the weight of Fe₂O₃ component alone.