Effect of Friction Stir Processing on Gas Tungsten Arc-Welded and Friction Stir-Welded 5083-H111 Aluminium Alloy Joints

<table class="table-group" id="tab3"><tr><td><table class="table"><tr><td class="thead-hr" colspan="4"><hr/></td></tr><tr class="thead"><td class="align_left">Welding current (A)</td><td class="align_center">Shielding gas flowrate (l/min)</td><td class="align_center">Voltage (V)</td><td class="align_center">Travel speed (mm/min)</td></tr><tr><td class="thead-hr" colspan="4"><hr/></td></tr><tr><td class="align_left">200</td><td class="align_center">15</td><td class="align_center">16</td><td class="align_center">150</td></tr><tr class="table-tr"><td colspan="4"><hr class="tbody-hr"/></td></tr></table></td></tr></table>

Advances in Materials Science and Engineering

tab3

Table 3

Table 3: Effect of Friction Stir Processing on Gas Tungsten Arc-Welded and Friction Stir-Welded 5083-H111 Aluminium Alloy Joints 