Hydrogen Effect on Cumulation of Failure, Mechanical Properties, and Fracture Toughness of Ni-Cr Alloys

Figure 1

The effect of rising K rate dK/dt on fracture toughness K_c in hydrogen under pressure 30 MPa of hydrogenated specimens of 20 mm thickness. The numbers near to curves correspond to ordinal numbers in Table 2.