Compression Performance of Newly Designed Replaceable Tubular Steel Piers
Table 2
Test results of steel material specimens.
| Label of material specimens | Thickness (mm) | Yield strength (MPa) | Tensile strength (MPa) | Rate of elongation (%) |
| 8 mm | Q345-1 | 8.0 | 323 | 408 | 14.5 | Q345-2 | 7.7 | 357 | 448 | 17.3 | Q345-3 | 7.7 | 355 | 453 | 15.3 | Average | 7.8 | 345 | 436 | 15.7 | Standard deviation | 0.141 | 15.578 | 20.138 | 1.178 |
| 14 mm | Q345-1 | 13.8 | 355 | 466 | 18.5 | Q345-2 | 14.1 | 360 | 468 | 17.6 | Q345-3 | 14.1 | 378 | 492 | 16.3 | Average | 14.0 | 364 | 475 | 17.5 | Standard deviation | 0.141 | 9.877 | 11.813 | 0.903 |
| 10 mm | LYP100-1 | 10.2 | 149 | 254 | 33.1 | LYP100-2 | 9.9 | 160 | 253 | 24.3 | LYP100-3 | 9.8 | 152 | 268 | 27.8 | Average | 10.0 | 154 | 258 | 28.4 | Standard deviation | 0.170 | 4.643 | 6.848 | 3.618 |
| 10 mm | LYP160-1 | 10.1 | 162 | 249 | 30.7 | LYP160-2 | 10.1 | 160 | 248 | 34.4 | LYP160-3 | 9.8 | 175 | 266 | 35.1 | Average | 10.0 | 166 | 254 | 33.4 | Standard deviation | 0.141 | 6.650 | 8.260 | 1.930 |
|
|