Combined Technology for the Parts Recovery Operating in Stress Factor Conditions

Table 6

Experimental data characterizing the microplastic deformation of deposited samples of steel 530H40 after annealing (group I).

σi (MPa)	Deformation			Deformation rms deviation			Deformation variation coefficient (%)
				S1	S2	S3	γ1	γ2	γ3
60.7	0.015984	0.025678	0.026	0.018	0.029	0.024	59.8	59.4	50.1
123	0.023255	0.025846	0.034033	0.027	0.035	0.024	68.5	68.1	70.7
186	0.030082	0.027925	0.034880	0.033	0.042	0.028	71.9	80.3	71
244	0.032564	0.030556	0.035800	0.041	0.045	0.029	79.8	112.9	73.9
305	0.033239	0.035679	0.036192	0.041	0.045	0.029	81.2	125.3	80.1
366	0.039689	0.042874	0.037646	0.048	0.047	0.029	101.3	137.4	81.2
427	0.041734	0.045840	0.039218	0.084	0.075	0.0306	131.1	235.6	92.3
488	0.051	0.056	0.041	0.088	0.103	0.032	201.2	240.7	238
528	0.057	0.066	0.043296	0.216	0.108	0.081	322.7	290.1	466.5
538	0.066929	0.079	0.044793	0.2780	0.187	0.209	500.5	302.2	487.2
602	0.070	0.101894	0.045	0.6305	0.308	0.303	705.4	524.1	868.6