Combined Technology for the Parts Recovery Operating in Stress Factor Conditions

Table 7

Experimental data characterizing the microplastic deformation of the deposited samples of steel 530H40 after heat treatment according to mode II (group II).

σi (MPa)	Deformation			Deformation rms deviation			Deformation variation coefficient (%)
				S1	S2	S3	γ1	γ2	γ3
59	0.007	0.005313	0	0.006	0.0056	0	25	0	0
119	0.008	0.006	0.001493	0.006	0.00604	0	69	70	0
188	0.008329	0.008	0.008	0.011	0.007	0.000504	75	70	63
240.2	0.010599	0.009175	0.009	0.013	0.0173	0.0067	80	89.8	68
300	0.010668	0.009833	0.009091	0.021	0.018	0.011	85	100	74
359	0.0133301	0.013591	0.010165	0.021	0.021	0.017	122	117	96
419	0.016631	0.016632	0.013132	0.023	0.023	0.021	132	131	122
481	0.017676	0.019566	0.016879	0.024	0.024	0.022	135	150	167
537	0.0226523	0.025	0.017148	0.027	0.025	0.023	154	183	207
601	0.026	0.030271	0.023797	0.035	0.034	0.035	162	250	266
659	0.032868	0.033985	0.024	0.036	0.045	0.035	196	490	1008
718	0.055	0.065	0.032216	0.055	0.055	0.038	270	571	2545