Tribological Behavior and Analysis on Surface Roughness of CNC Milled Dual Heat Treated Al6061 Composites

Table 7

Deform 3D simulation values of effective stress (von Mises) and displacement.

Step No.	HSS-COLD-2500	HSS-HOT-3800	WC-COLD-2500	WC-HOT-3800
Effective stress (MPa)
1	1910	1810	1830	2420
10	2190	2540	2030	2430
20	1780	2580	1990	1830
30	2490	2660	2250	2270
40	1940	1910	1810	1480
50	1810	2350	2300	2290
60	2500	2260	1880	2900
70	2300	2410	2810	2530
80	1980	2280	3050	2090
90	1960	2220	1990	1230
100	1820	1950	1910	1720
110	1960	2260	2560	2760
120	1880	2040	1880	2060
130	2050	2180	2140	1880
140	2120	2160	1510	2080
150	1990	1580	1880	1980
160	1960	1940	2100	2520
170	1730	2570	2010	2160
180	1910	2390	2070	2020
190	1730	2320	2280	2150
200	2050	1970	2430	2340
Displacement (mm)
1	4.24	2.16	1.33	4.46
10	7.96	8.11	9.14	7.92
20	5.3	5.09	4.93	6.01
30	5.53	5.95	4.47	5.88
40	5.08	5.58	4.47	5.68
50	6.87	5.39	5.33	5.73
60	7.05	5.9	5.75	5.73
70	5.84	5.24	5.76	5.73
80	6.08	4.91	5.11	5.73
90	5.9	6.83	5.12	5.73
100	5.58	5.24	5.76	5.73
110	6.41	6.02	5.57	5.74
120	5.8	6.04	5.51	5.74
130	5.79	5.49	5.51	7.06
140	5.51	5.49	5.38	5.74
150	5.25	5.4	6.03	7.3
160	7.64	6.62	6.97	7.29
170	6	5.74	5.7	7.3
180	6.04	5.39	6.17	7.3
190	5.5	5.9	6.99	6.22
200	5.66	6.58	6	6.43