Investigation of Drilling Process Parameters of Palmyra Based Composite
Table 2
Thrust force generated by the candlestick, standard twist, and step cone drill bits during the drilling process.
| S. no | Resin | Speed (rpm) | Feed (mm/rev) | Thrust force by candlestick (N) | Thrust force by a twist drill | Thrust force by step cone drill |
| 1 | Epoxy | 1000 | 0.10 | 08.153 | 10.371 | 11.232 | 2 | Epoxy | 1000 | 0.15 | 09.292 | 10.674 | 11.331 | 3 | Epoxy | 1000 | 0.20 | 07.392 | 10.998 | 10.459 | 4 | Epoxy | 1500 | 0.10 | 10.169 | 10.370 | 12.981 | 5 | Epoxy | 1500 | 0.15 | 09.125 | 10.458 | 10.600 | 6 | Epoxy | 1500 | 0.20 | 10.023 | 10.566 | 10.968 | 7 | Epoxy | 2000 | 0.10 | 09.674 | 10.234 | 12.259 | 8 | Epoxy | 2000 | 0.15 | 10.359 | 10.356 | 12.657 | 9 | Epoxy | 2000 | 0.20 | 09.129 | 10.554 | 11.227 | 10 | Polyester | 1000 | 0.1 | 09.627 | 10.369 | 11.599 | 11 | Polyester | 1000 | 0.15 | 10.522 | 10.273 | 11.451 | 12 | Polyester | 1000 | 0.20 | 08.439 | 10.123 | 11.348 | 13 | Polyester | 1500 | 0.10 | 10.438 | 10.262 | 11.117 | 14 | Polyester | 1500 | 0.15 | 10.566 | 10.178 | 10.573 | 15 | Polyester | 1500 | 0.20 | 10.635 | 10.019 | 11.896 | 16 | Polyester | 2000 | 0.10 | 09.534 | 10.198 | 10.693 | 17 | Polyester | 2000 | 0.15 | 08.356 | 09.956 | 13.893 | 18 | Polyester | 2000 | 0.20 | 09.259 | 09.897 | 11.354 | 19 | Vinyl ester | 1000 | 0.10 | 08.933 | 10.595 | 11.400 | 20 | Vinyl ester | 1000 | 0.15 | 09.875 | 10.097 | 11.366 | 21 | Vinyl ester | 1000 | 0.20 | 08.996 | 09.899 | 10.289 | 22 | Vinyl ester | 1500 | 0.10 | 10.544 | 10.480 | 11.090 | 23 | Vinyl ester | 1500 | 0.15 | 09.153 | 10.569 | 11.199 | 24 | Vinyl ester | 1500 | 0.20 | 09.756 | 10.668 | 13.288 | 25 | Vinyl ester | 2000 | 0.10 | 09.432 | 10.393 | 12.639 | 26 | Vinyl ester | 2000 | 0.15 | 09.356 | 10.456 | 12.156 | 27 | Vinyl ester | 2000 | 0.20 | 08.289 | 09.754 | 10.887 |
|
|