Artificial Neural Network Modeling of Abrasion Loss and Surface Roughness of Crab Carapace Impregnated Coir Vinyl Ester Composites

Table 2

Experimental results for carapace filler-filled coir vinyl ester composites.

Sample specimen	Fiber length (mm)	Fiber diameter (mm)	Filler content (%)	Abrasion loss	Surface roughness
1	10	0.1	0	680	0.256
2	10	0.18	0	675	0.336
3	10	0.2	0	690	0.268
4	10	0.1	2	598	0.276
5	10	0.18	2	610	0.443
6	10	0.2	2	636	0.378
7	10	0.1	4	685	0.373
8	10	0.18	4	681	0.487
9	10	0.2	4	670	0.498
10	30	0.1	0	690	0.281
11	30	0.18	0	675	0.485
12	30	0.2	0	655	0.411
13	30	0.1	2	676	0.379
14	30	0.18	2	659	0.495
15	30	0.2	2	700	0.393
16	30	0.1	4	620	0.395
17	30	0.18	4	610	0.55
18	30	0.2	4	640	0.515
19	50	0.1	0	558	0.321
20	50	0.18	0	531	0.418
21	50	0.2	0	541	0.398
22	50	0.1	2	591	0.279
23	50	0.18	2	565	0.225
24	50	0.2	2	603	0.287
25	50	0.1	4	579	0.387
26	50	0.18	4	566	0.381
27	50	0.2	4	590	0.298