Study on Coercivity-Stress Relationship of X80 Steel under Biaxial Stress
Table 4
Error analysis of fitting results of test piece 2.
| Serial no. | (MPa) | (MPa) | (A/m) | (A/m) | (A/m) | (%) | Hcy (A/m) | Hc'y (A/m) | (A/m) | (%) |
| 1 | 0 | 0 | 1079.1 | 1043 | 36.1 | 3.35 | 1089.6 | 1087.5 | 2.1 | 0.19 | 2 | 0 | 30 | 1086.4 | 1052.9 | 33.5 | 3.08 | 1071.5 | 1072.4 | −0.9 | −0.08 | 3 | 0 | 60 | 1092.4 | 1062.7 | 29.7 | 2.72 | 1060.1 | 1057.4 | 2.7 | 0.25 | 4 | 0 | 90 | 1102.1 | 1072.6 | 29.5 | 2.68 | 1042.1 | 1042.5 | −0.4 | −0.04 | 5 | 0 | 120 | 1113.2 | 1082.5 | 30.7 | 2.76 | 1010.7 | 1027.4 | −16.7 | −1.65 | 6 | 0 | 150 | 1119.2 | 1092.4 | 26.8 | 2.39 | 1007 | 1012.8 | −5.8 | −0.58 | 7 | 0 | 180 | 1125.3 | 1102.2 | 23.1 | 2.05 | 996.6 | 997.6 | −1.0 | −0.10 | 8 | 0 | 210 | 1143.6 | 1112.1 | 31.5 | 2.75 | 994.1 | 982.7 | 11.4 | 1.15 | 9 | 0 | 240 | 1176.2 | 1122 | 54.2 | 4.61 | 984.9 | 967.2 | 17.7 | 1.80 | 10 | 180 | 0 | 998.1 | 1132 | −133.9 | −13.42 | 1129.9 | 1134.5 | −4.6 | −0.41 | 11 | 180 | 30 | 997.2 | 1141.9 | −144.7 | −14.51 | 1117.1 | 1119.6 | −2.5 | −0.22 | 12 | 180 | 60 | 996.3 | 1151.7 | −155.4 | −15.60 | 1104.3 | 1104.8 | −0.5 | −0.05 | 13 | 180 | 90 | 1013.9 | 1161.6 | −147.7 | −14.57 | 1092.7 | 1089.1 | 3.6 | 0.33 | 14 | 180 | 120 | 1031.4 | 1171.5 | −140.1 | −13.58 | 1081.2 | 1074.5 | 6.7 | 0.62 | 15 | 180 | 150 | 1072.8 | 1181.4 | −108.6 | −10.12 | 1059.5 | 1059 | 0.5 | 0.05 | 16 | 180 | 180 | 1114.3 | 1191.2 | −76.9 | −6.90 | 1037.9 | 1044.5 | −6.6 | −0.64 | 17 | 180 | 210 | 1114.2 | 1201.1 | −86.9 | −7.80 | 1023.7 | 1029.9 | −6.2 | −0.61 | 18 | 180 | 240 | 1114.1 | 1211 | −96.9 | −8.70 | 1009.5 | 1014.6 | −5.1 | −0.51 |
|
|