An Investigation on Effects by Adding Cerium and Lithium on Mechanical and Metallurgical Properties of AZ91D + XCe + XLi Cast Mg Alloy
Table 2
Corrosion Rates for different experimental alloys.
| Experimental alloys | Weight loss (g) | Density (gm/cc) | K Factor | Area (cm2) | ∗TOE (h) | Corrosion rate (mm/year) |
| AZ91D + 0 wt.%Li + 0wt.%Ce | 0.201 | 1.777 | 8.76 × 104 | 7.8 | 72 | 17.64353635 | AZ91D + 0.5wt.%Li + 0.5wt.%Ce | 0.004 | 1.7664 | 8.76 × 104 | 5.7 | 72 | 0.48335664 | AZ91D + 0.5wt.%Li + 1.0wt.%Ce | 0.068 | 1.7762 | 8.76 × 104 | 6.3 | 72 | 7.393466463 | AZ91D + 0.5wt.%Li + 2.0wt.%Ce | 0.096 | 1.7764 | 8.76 × 104 | 3.66 | 72 | 17.96474235 | AZ91D + 1.0wt.%Li + 0.5wt.%Ce | 0.201 | 1.781 | 8.76 × 104 | 7.81 | 72 | 17.58137 | AZ91D + 1.0wt.%Li + 1.0wt.%Ce | 0.003 | 1.7824 | 8.76 × 104 | 5.17 | 72 | 0.396092982 | AZ91D + 1.0wt.%Li + 2.0wt.%Ce | 0.011 | 1.7832 | 8.76 × 104 | 6.13 | 72 | 1.224344867 | AZ91D + 2.0wt.%Li + 0.5wt.%Ce | 0.016 | 1.7864 | 8.76 × 104 | 3.62 | 72 | 3.010262107 | AZ91D + 2.0wt.%Li + 1.0wt.%Ce | 0.02 | 1.787 | 8.76 × 104 | 6.31 | 72 | 2.157981383 | AZ91D + 2.0wt.%Li + 2.0wt.%Ce | 0.024 | 1.7884 | 8.76 × 104 | 3.56 | 72 | 4.586360541 |
|
|
∗TOE: time of exposure.
|