Structure and Mechanical Properties of Titanium Processed by Twist Extrusion and Subsequent Rolling

Figure 6

The change of the accumulated logarithmic degree of the deformation at the first stage of billet rolling after TE in passage groups: temperature range of rolling is 350°C–200°С; there are 3 reductions in 1 passing after 1 heating; change in billet thickness during rolling is 24–9.7 mm.