High-Temperature Creep Behavior of a Nickel-Based Single-Crystal Superalloy with Small-Angle Deviation from [111] Orientation
Figure 5
Dislocation configuration after the creep fracture at 1040°C/137 MPa: (a) , (b) , (c) , and (d) .