Microstructure and Stress Rupture Properties of K417G Superalloy at Different Hot Isostatic Pressing Temperatures

<div>TEM micrographs of the K417G alloy after the stress rupture test at 760°C and 645 MPa. Primary <i>γ</i>′ phase particles sheared by dislocations (a) and (b) fine <i>γ</i>′ phase particles surrounded by the Orowan loop.</div>

Advances in Materials Science and Engineering

fig13

Figure 13

Figure 13: Microstructure and Stress Rupture Properties of K417G Superalloy at Different Hot Isostatic Pressing Temperatures 