Electrodeposition of Hydroxyapatite-Multiwalled Carbon Nanotube Nanocomposite on Ti6Al4V
Table 1
Mass, thickness, and adhesion of HAp-MWCNTs synthesized at different potential ranges.
| | Potential range (V/SCE) | Mass (mg/cm2) | Thickness (μm) ISO 4288-1998 | Adhesion (MPa) |
| | 0 ÷ −1.4 | — | — | — | | 0 ÷ −1.5 | — | — | — | | 0 ÷ −1.6 | 1.32 ± 0.04 | 4.0 ± 0.74 | 12.2 ± 0.52 | | 0 ÷ −1.7 | 1.43 ± 0.03 | 4.3 ± 0.62 | 11.9 ± 0.80 | | 0 ÷ −1.8 | 1.64 ± 0.02 | 4.9 ± 0.85 | 11.6 ± 0.42 | | 0 ÷ −1.9 | 1.88 ± 0.02 | 5.7 ± 0.94 | 11.0 ± 0.35 | | 0 ÷ −2.0 | 2.08 ± 0.03 | 6.3 ± 1.00 | 10.4 ± 0.50 | | 0 ÷ −2.1 | 2.33 ± 0.05 | 7.0 ± 1.04 | 7.4 ± 0.72 |
|
|