Research Article
Flexural Strength of Vitreous Ceramics Based on Lithium Disilicate and Lithium Silicate Reinforced with Zirconia for CAD/CAM
Table 2
Parameters used in the crystallization of the samples.
| | G1 | G3 | G4 | G5 |
| Predrying | 2 min | — | — | — | Drying | 2 min | — | — | — | Preheating | 2 min | — | — | — | Starting temperature (°C) | 500 | 403 | 400 | 400 | Temperature increase | 55°C/min | t1 90°C/min t2 30°C/min | 55°C/min | 60°C/min | Burning temperature | — | T1 820°C T2 840°C | T 840°C | T 840°C | Final temperature | 820°C | — | — | 700°C | Vacuum | Off | Vacuum1: 550°C; e 1022°C Vacuum2: 820°C; e 1508°C | Vacuum1: 410°C Vacuum2: 840°C | On: 550°C Off: 840°C | Waiting time | 1.5 min | — | 4 min | — | Closing time | — | 6 min | — | — | Maintenance time | — | H1: 10 sec H2: 7 min | 8 min | 10 min | Cooling rate (°C/min) | 3 min | — | — | — |
|
|