On the Stress Corrosion Cracking and Hydrogen Embrittlement Behavior of Austenitic Stainless Steels in Boiling Saturated Magnesium Chloride Solutions

Figure 5

Fracture appearances for (a) type 304 at 𝑇=416 K and 𝜎=300 MPa; x550 (b) for type 310 at 𝑇=416 K and 𝜎=300 MPa; x650, (c) for type 316 at 𝑇=408K and 𝜎=300 MPa; x550 and (d) for type 316 at 𝑇=408 K and 𝜎=400 MPa; x1000 in boiling saturated MgCl₂ solutions.

(a)

(b)

(c)

(d)