Sodium Citrate as an Environmentally Friendly Corrosion Inhibitor of Steel in a Neutral Environment
Table 3
Impedance characteristics of 09G2S steel after exposure to 0.1% NaCl solution with different concentrations of sodium citrate.
| (g/l) | (ohms⋅cm2) | (ohms⋅cm2) | (/ohms⋅cm2) | | 3 hours | 24 hours | 3 hours | 24 hours | 3 hours | 24 hours | 3 hours | 24 hours |
| 0 | 206 | 192 | 866 | 836 | | | 0.71 | 0.66 | 1.0 | 155 | 164 | 1540 | 1257 | | | 0.73 | 0.55 | 1.5 | 122 | 133 | 2323 | 1313 | | | 0.79 | 0.64 | 2.0 | 114 | 116 | 2269 | 1694 | | | 0.74 | 0.60 | 2.5 | 99 | 110 | 2677 | 1859 | | | 0.73 | 0.65 |
|
|