Hydrodynamic Cavitation-Assisted Synthesis of Nanocalcite
Figure 4
Effect of different experimental conditions on X-ray diffraction spectra. A: Without orifice, 4% Ca(OH)2 slurry, 5 l/min CO2 flow rate; B: 1 mm orifice, 4% Ca(OH)2, slurry 5 l/min CO2 flow rate; C: 2 mm orifice 4% Ca(OH)2, slurry 5 l/min CO2 flow rate; D: 3 mm orifice 4% Ca(OH)2 slurry 5 l/min CO2 flow rate; E: 4 mm orifice 4% Ca(OH)2, slurry 7 l/min CO2 flow rate; F: 4 mm orifice 2% Ca(OH)2, slurry 5 l/min CO2 flow rate; G: 4 mm orifice 6% Ca(OH)2 slurry, 5 l/min CO2 flow rate; H: 4 mm orifice 4% Ca(OH)2 slurry, 3 CO2 l/min flow rate; I: 4 mm orifice, 4% Ca(OH)2 slurry, 5 CO2 l/min flow rate.