Bonding Characteristics of Macrosynthetic Fiber in Latex-Modified Fiber-Reinforced Cement Composites as a Function of Carbon Nanotube Content

<table class="figure-group"><tr class="fig-image" id="a"><td><object data="https://static-preview.hindawi.com/articles/ijps/volume-2016/7324975/figures/7324975.fig.005a.svgz" name="7324975.fig.005a" type="image/svg+xml"></object></td></tr><tr class="fig-caption"><td><b>(a) </b>Bond strength</td></tr><tr class="fig-image" id="b"><td><object data="https://static-preview.hindawi.com/articles/ijps/volume-2016/7324975/figures/7324975.fig.005b.svgz" name="7324975.fig.005b" type="image/svg+xml"></object></td></tr><tr class="fig-caption"><td><b>(b) </b>Interface toughness</td></tr></table>

<div>Bond strength and interface toughness of macrosynthetic fiber in LMHFRCCs.</div>

International Journal of Polymer Science

fig5

Figure 5

Figure 5: Bonding Characteristics of Macrosynthetic Fiber in Latex-Modified Fiber-Reinforced Cement Composites as a Function of Carbon Nanotube Content 

Figure 5 | Bonding Characteristics of Macrosynthetic Fiber in Latex-Modified Fiber-Reinforced Cement Composites as a Function of Carbon Nanotube Content 