Comparative Study of Structural, Electrical, and Magnetic Behaviour of Ni-Cu-Zn Nanoferrites Sintered by Microwave and Conventional Techniques

Table 1

Lattice parameter, X-ray density, experimental density, crystallite size, and resistivity values of ferrites.

Samples “x”	Lattice parameter (Å)	X-ray density (gm/cm^3)	Experimental density (gm/cm^3)	Crystallite size (nm)	Resistivity (Ω-cm)
	MW	MW	MW	MW	MW	Con
0.0	8.356	5.37	2.29	35.30	6.83 × 10^7	4.35 × 10^7
0.1	8.362	5.37	2.58	36.84	4.44 × 10^7	6.28 × 10^7
0.2	8.363	5.38	3.00	36.20	4.83 × 10^7	1.85 × 10^7
0.3	8.369	5.38	3.34	34.26	3.34 × 10^7	2.32 × 10^7
0.4	8.372	5.38	3.48	31.57	5.37 × 10^7	5.39 × 10^6
0.5	8.375	5.39	3.30	32.65	2.13 × 10^7	4.14 × 10^6