Effects of Sintering Temperature on the Morphology and Photoluminescence of Eu³⁺ Doped Zinc Molybdenum Oxide Hydrate

Table 1

Lattice parameters of Eu³⁺ doped Zn₅Mo₂O₁₁·5H₂O and Eu³⁺ doped ZnMoO₄ determined by whole pattern fitting and Rietveld refinement.

Precursor	(nm)	(nm)	(nm)	α (°)	β (°)	γ (°)	Phase
As-prepared	0.6100	0.6100	2.164	90	90	120	Zn5Mo2O11·5H2O
Annealed at 200°C	0.6110	0.6110	2.163	90	90	120	Zn5Mo2O11·5H2O
Annealed at 400°C	0.8372	0.9702	0.6964	106.80	101.81	96.80	Triclinic ZnMoO4
Annealed at 600°C	0.8364	0.9689	0.6960	106.86	101.77	96.75	Triclinic ZnMoO4
Annealed at 800°C	0.8353	0.9673	0.6954	106.84	101.76	96.73	ZnMoO4 (primary)