Effects of Boron Nitride Coatings at High Temperatures and Electromagnetic Wave Absorption Properties of Carbon Fiber-Based Magnetic Materials
Table 1
Composition of the prepared composite samples with PAN-based preoxidative felt, FeCl3, CoSO4, NiSO4, H3BO3, and CO(NH2)2.
| | Sample code | Base matrix (PAN-based preoxidative felt) quality (g) | Impregnation solution (mol L-1) | | Solution 1 | Solution 2 | | FeCl3 | CoSO4 | NiSO4 | H3BO3 | CO(NH2)2 |
| | Carbon fiber (CF) | 12 | 0.000 | 0.000 | 0.000 | 0.000 | 0.000 | | CF/1FeCoNi | 12 | 0.250 | 0.250 | 0.125 | 0.000 | 0.000 | | CF/1.5FeCoNi | 12 | 0.375 | 0.375 | 0.1875 | 0.000 | 0.000 | | CF/2.5FeCoNi | 12 | 0.625 | 0.625 | 0.3125 | 0.000 | 0.000 | | CF/1FeCoNi/2BN | 12 | 0.250 | 0.250 | 0.125 | 1.000 | 3.000 | | CF/2.5FeCoNi/2BN | 12 | 0.625 | 0.625 | 0.3125 | 1.000 | 3.000 | | CF/1.5FeCoNi/1BN | 12 | 0.375 | 0.375 | 0.1875 | 0.500 | 1.500 | | CF/1.5FeCoNi/2BN | 12 | 0.375 | 0.375 | 0.1875 | 1.000 | 3.000 | | CF/1.5FeCoNi/3BN | 12 | 0.375 | 0.375 | 0.1875 | 1.500 | 4.500 |
|
|