[Retracted] Experimental Study on Surface Roughness and Flank Wear in Turning of Nimonic C263 under Dry Cutting Conditions

Table 3

Results from both experimental and RSM-modeled studies.

S. No.	Controlling factors			Experimental values		RSM values		% age error expt. vs. RSM
				(μm)	VB (mm)	(μm)	VB (mm)	(μm)	VB (mm)
1	80	0.055	0.25	2.55	0.30	2.51	0.301	1.56	0.33
2	80	0.055	0.50	2.2	0.32	2.34	0.317	5.98	0.93
3	80	0.055	0.75	2.35	0.34	2.18	0.338	7.23	0.58
4	80	0.096	0.25	2.8	0.33	2.88	0.329	3.04	0.30
5	80	0.096	0.50	2.6	0.35	2.71	0.348	4.05	0.57
6	80	0.096	0.75	2.4	0.36	2.56	0.372	6.25	3.22
7	80	0.159	0.25	3.1	0.38	3.02	0.362	0.33	4.73
8	80	0.159	0.50	3	0.39	2.87	0.385	4.33	1.28
9	80	0.159	0.75	2.8	0.40	2.73	0.413	2.50	3.14
10	125	0.055	0.25	2.25	0.29	2.18	0.291	3.11	0.34
11	125	0.055	0.50	2.1	0.31	2.00	0.306	4.76	1.29
12	125	0.055	0.75	1.7	0.33	1.85	0.326	8.10	1.21
13	125	0.096	0.25	2.65	0.30	2.67	0.315	0	4.76
14	125	0.096	0.50	2.55	0.345	2.49	0.333	0.74	3.47
15	125	0.096	0.75	2.65	0.365	2.34	0.356	11	2.46
16	125	0.159	0.25	2.93	0.32	2.96	0.342	1.01	6.43
17	125	0.159	0.50	2.6	0.36	2.80	0.364	7.14	1.09
18	125	0.159	0.75	2.5	0.41	2.66	0.391	6.05	4.63
19	190	0.055	0.25	1.6	0.42	1.76	0.393	9.09	6.42
20	190	0.055	0.50	1.65	0.38	1.58	0.407	4.24	6.63
21	190	0.055	0.75	1.45	0.42	1.41	0.426	2.75	1.40
22	190	0.096	0.25	2.65	0.39	2.43	0.412	8.30	5.33
23	190	0.096	0.50	2.15	0.45	2.25	0.429	4.44	4.66
24	190	0.096	0.75	1.9	0.46	2.09	0.451	9	1.95
25	190	0.159	0.25	2.8	0.45	2.94	0.430	4.7	4.44
26	190	0.159	0.50	2.95	0.44	2.77	0.451	6.10	2.43
27	190	0.159	0.75	2.7	0.47	2.62	0.477	2.96	1.46