Research Article
Mixed Interlaminar Fracture Toughness and Durability of Composites under Humid and Hot Conditions
Table 2
Composite material performance.
| | Material | Compound material |
| | Stretch | Strength (MPa) | 84.76 | Impact strength (kgcm/cm2) | 14.0 | Glass transition temperature (°C) | 218 | | Modulus (GPa) | 3.29 | | Elongation at break (%) | 3.34 | Heat distortion temperature (°C) | 198 | | Compression | Strength (MPa) | 167.18 | Fracture toughness GIC (J/m2) | 95 | Density (g/cm2) | 1.256 | | Bending | Strength (MPa) | 134.47 | | Modulus (GPa) | 3.66 | Saturated moisture absorption in boiling water (%) | 3.3 |
|
|