Artificial Intelligence Investigation on (Al-Si-Fe) Alloy Reinforced with Nanoceramic Particles by RSM

Table 3

Experimental values compared with predicted values from regression equations.

Taguchi L27 Array	Experimental values			Values predicted from regression equations
	COF	Sp. wear rate mm^3/Nm	Friction force ()	COF	Sp. wear rate mm^3/Nm	Friction force ()	Residuals
							COF	Sp. wear rate	Friction force
1	0.21	2.45	1.2	0.23	2.29	1.14	-0.02	0.15	0.05
2	0.21	2.45	1.2	0.23	2.2	1.14	-0.02	0.150	0.05
3	0.21	2.45	1.2	0.23	2.29	1.14	-0.028	0.150	0.05
4	0.26	0.61	2.6	0.27	1.25	3.16	-0.012	-0.64	-0.56
5	0.26	0.61	2.6	0.27	1.25	3.16	-0.012	-0.64	-0.56
6	0.26	0.61	2.6	0.27	1.25	3.16	-0.012	-0.64	-0.56
7	0.28	0.29	5.3	0.30	0.13	5.23	-0.028	0.151	0.06
8	0.28	0.29	5.3	0.30	0.13	5.23	-0.028	0.151	0.06
9	0.28	0.29	5.3	0.30	0.13	5.2	-0.028	0.15	0.06
10	0.22	0.53	1.98	0.15	0.46	1.34	0.069	0.06	0.63
11	0.21	0.51	1.5	0.15	0.46080	1.34	0.059	0.049	0.15
12	0.21	0.52	1.5	0.15	0.46	1.34	0.059	0.05	0.15
13	0.06	0.98	1.5	0.16	0.87	2.34	-0.10	0.10	-0.84
14	0.26	0.98	2.6	0.16	0.87	2.34	0.096	0.10	0.25
15	0.26	0.97	2.6	0.16	0.87	2.34	0.096	0.099	0.25
16	0.01	1.72	1.98	0.21	1.2	3.5	-0.20	0.51	-1.54
17	0.63	1.74	7.43	0.21	1.20	3.52	0.411	0.53	3.9
18	0.15	1.73	3.2	0.21	1.20	3.52	-0.06	0.523	-0.32
19	0.01	0.31	0.5	0.04	0.15	0.46	-0.030	0.159	0.03
20	0.03	0.35	0.8	0.04	0.15	0.46	-0.010	0.199	0.33
21	0.01	0.33	0.8	0.04	0.15	0.46	-0.030	0.17	0.33
22	0.06	0.16	1.1	0.09	0.41	1.70	-0.035	-0.250	-0.60
23	0.06	0.17	1.1	0.09	0.41	1.70	-0.035	-0.240	-0.60
24	0.05	0.19	1.3	0.09	0.41	1.70	-0.045	-0.220	-0.40
25	0.07	0.52	2.1	0.10	0.82	2.70	-0.039	-0.30	-0.60
26	0.11	0.53	2.3	0.10	0.82	2.70	0.00063	-0.290	-0.40
27	0.13	0.55	3.32	0.10	0.82	2.70	0.020	-0.27	0.61