Research Article
Multiobjective Optimization of Injection Molding Process Parameters for the Precision Manufacturing of Plastic Optical Lens
Table 2
Experimental results and S/N ratio of HR and PV20.
| Number | IMPP | HR (% | PV20 (µm | S/N ratio (dB | | | | | | | | | HR | PV20 |
| | 230 | 60 | 90 | 5.2 | 4 | 110 | 90 | 25 | 8.23 | 1.102 | −18.3080 | −0.8436 | | 220 | 70 | 90 | 5.4 | 8 | 110 | 60 | 15 | 5.31 | 1.721 | −14.5019 | −4.7156 | | 220 | 80 | 100 | 5.2 | 8 | 100 | 60 | 25 | 6.06 | 0.813 | −15.6495 | 1.7982 | | 220 | 60 | 100 | 5.6 | 8 | 110 | 90 | 35 | 8.85 | 0.871 | −18.9389 | 1.1996 | | 230 | 80 | 100 | 5.4 | 4 | 100 | 90 | 15 | 12.22 | 1.41 | −21.7414 | −2.9844 | | 220 | 80 | 90 | 5.6 | 6 | 90 | 90 | 15 | 11.87 | 1.523 | −21.4890 | −3.6540 | | 220 | 60 | 90 | 5.4 | 6 | 100 | 75 | 25 | 6.05 | 0.321 | −15.6351 | 9.8699 | | 220 | 70 | 100 | 5.6 | 4 | 90 | 75 | 25 | 8.67 | 0.512 | −18.7604 | 5.8146 | | 220 | 60 | 80 | 5.2 | 4 | 90 | 60 | 15 | 4.85 | 1.825 | −13.7148 | −5.2253 | | 230 | 80 | 80 | 5.6 | 6 | 110 | 60 | 25 | 4.65 | 0.995 | −13.3491 | 0.0435 | | 230 | 60 | 80 | 5.6 | 8 | 100 | 75 | 15 | 6.32 | 0.804 | −16.0143 | 1.8949 | 2 | 230 | 60 | 100 | 5.4 | 6 | 90 | 60 | 35 | 7.89 | 1.381 | −17.9415 | −2.8039 | | 220 | 70 | 80 | 5.2 | 6 | 100 | 90 | 35 | 8.31 | 0.482 | −18.3920 | 6.3391 | | 220 | 80 | 80 | 5.4 | 4 | 110 | 75 | 35 | 4.01 | 0.782 | −12.0629 | 2.1359 | | 230 | 70 | 90 | 5.6 | 4 | 100 | 60 | 35 | 6.11 | 0.873 | −15.7208 | 1.1797 | | 230 | 80 | 90 | 5.2 | 8 | 90 | 75 | 35 | 8.34 | 0.672 | −18.4233 | 3.4526 | | 230 | 70 | 80 | 5.4 | 8 | 90 | 90 | 25 | 9.68 | 1.363 | −19.7175 | −2.6899 | | 230 | 70 | 100 | 5.2 | 6 | 110 | 75 | 15 | 7.02 | 0.945 | −16.9267 | 0.4914 |
|
|