Effect of the Different High Volume Fraction of SiC Particles on the Junction of Bismuthate Glass-SiC<sub>p</sub>/Al Composite

<div>XRD patterns of the bismuthate glass, SiC powders, 6061Al matrix, and the fabricated <svg height="14.067pt" id="M28" style="vertical-align:-5.3006pt" version="1.1" viewbox="-0.0498162 -8.7664 23.7567 14.067" width="23.7567pt" xmlns="http://www.w3.org/2000/svg" xmlns:xlink="http://www.w3.org/1999/xlink"><g transform="matrix(.013,0,0,-0.013,0,0)"><path d="M409 504C401 567 396 607 392 642C354 654 312 665 266 665C137 665 60 583 60 487C60 374 161 325 225 290C300 250 355 215 355 141C355 68 311 21 235 21C131 21 86 122 71 183L41 176C48 128 61 42 68 21C78 16 93 8 118 0C142 -7 175 -15 216 -15C349 -15 438 69 438 174C438 287 344 333 265 374C186 414 138 449 138 522C138 576 172 631 249 631C336 631 363 562 380 499L409 504Z" id="g121-81"></path></g><g transform="matrix(.013,0,0,-0.013,6.084,0)"><path d="M135 536C164 536 186 560 186 587C186 617 164 639 136 639C109 639 85 617 85 587C85 560 109 536 135 536ZM252 0V26C188 32 181 38 181 106V451C138 433 90 420 39 412V388C99 379 102 374 102 312V106C102 38 95 32 32 26V0H252Z" id="g121-103"></path></g><g transform="matrix(.013,0,0,-0.013,9.568,0)"><path d="M614 175C564 76 510 21 408 21C256 21 146 149 146 336C146 488 235 629 402 629C510 629 570 586 597 480L626 488C620 541 614 582 606 638C578 643 510 665 429 665C206 665 44 527 44 316C44 157 153 -15 402 -15C474 -15 558 5 586 11C604 45 629 119 643 165L614 175Z" id="g121-65"></path></g><g transform="matrix(.0091,0,0,-0.0091,18.213,3.132)"><path d="M173 382V461C125 442 68 425 25 418V390C88 382 92 382 92 317V-127C92 -191 84 -199 18 -204V-235H259V-204C180 -196 173 -192 173 -120V7C188 -1 212 -11 243 -12C375 12 495 109 495 261C495 361 427 451 316 451C303 451 283 446 266 435L173 382ZM173 345C200 365 243 388 274 388C346 388 409 329 409 222C409 111 353 40 266 40C231 40 196 56 173 79V345Z" id="g58-110"></path></g></svg>/6061Al composites.</div>

Scanning

fig4

Figure 4

Figure 4: Effect of the Different High Volume Fraction of SiC Particles on the Junction of Bismuthate Glass-SiC<sub>p</sub>/Al Composite 

Scanning

Effect of the Different High Volume Fraction of SiC Particles on the Junction of Bismuthate Glass-SiCp/Al Composite

Figure 4

Effect of the Different High Volume Fraction of SiC Particles on the Junction of Bismuthate Glass-SiC_p/Al Composite