Preparation of Magnetic Composite Polyaniline/Fe<sub>3</sub>O<sub>4</sub>−Hydrotalcite and Performance in Removal of Methyl Orange

Tran, Thi Tuong An; Duong, Huynh Thanh Linh; Pham, Thi Thuy Phuong; Nguyen, Tri; Nguyen, Thi Dung; Tran, Boi An

doi:https://doi.org/10.1155/2021/4150073

Adsorption Science & Technology

On this page

Abstract Introduction Results and Discussion Conclusion Data Availability Conflicts of Interest Acknowledgments References Copyright Related Articles

Research Article | Open Access

Volume 2021 | Article ID 4150073 | https://doi.org/10.1155/2021/4150073

Preparation of Magnetic Composite Polyaniline/Fe₃O₄−Hydrotalcite and Performance in Removal of Methyl Orange

Thi Tuong An Tran,¹Huynh Thanh Linh Duong,²Thi Thuy Phuong Pham,²Tri Nguyen,²Thi Dung Nguyen,²and Boi An Tran²

Academic Editor: S Rangabhashiyam

Received29 Jul 2021

Revised26 Aug 2021

Accepted29 Oct 2021

Published01 Dec 2021

Abstract

Magnetic composite fabricated from polyaniline and Fe₃O₄-hydrotalcite (Pan/MHT) was successfully applicated for removal of methyl orange (MO) from wastewater. The structure and properties of Pan/MHT were characterized by Fourier-transform infrared spectroscopy, scanning electron microscopy, X-ray diffraction, vibrating sample magnetometer, and Brunauer-Emmett-Teller adsorption isotherm. Adsorption kinetic results indicated that the adsorption process followed pseudosecond-order kinetic model (), MO adsorption onto Pan/MHT was well described by Freundlich isotherm (), and the MO adsorption capacity of 2 Pan/MHT obtained the highest with . Batch adsorption experiments were carried out using magnetic composite with the effects of initial MO concentration, solution pH, and adsorbent dosage. The results revealed that the magnetic Pan/MHT exhibited efficient adsorption of MO in the aqueous solution as a result of the affinity for organic dyes, microporous structure, and suitable surface area for adsorption (15,460 m²/g). The superparamagnetic behavior of Pan/MHT (with, , and) helps that it could be separated from the solution and performs as an economical and alternative adsorbent to removal and degrade azo dye from wastewater. Pan/MHT was also investigated to reuse after desorption of MO in 0.1 M HCl, and the results show that 2 Pan/MHT can be reused for 4 cycles with

1. Introduction

Dyes are widely used in many fields, such as textile, cosmetic, pigment, paper industry, dyeing, or tanning industry. In particular, textile industry wastewater contains a lot of dyes with large molecule structure including the azo group which is sustainable and difficult to decompose [1]. The presence of organic dyes is a main cause of environmental pollution problems because they are nonbiodegradable; so, an effective method is necessary to remove them from wastewater sources. It is estimated that 10-15% lost in the effluent during the dyeing process [2]. If they are not promptly treated strictly before releasing to the environment, they can destroy the ecosystem of aquatic organisms and threaten the self-cleaning capacity of the receiving source and the human life.

In recent years, there are many applications for treatment such as membrane filtration, redox, electrochemical, adsorption, and biological methods. Among them, adsorption is the popular method because of its efficiency and economy. The adsorbents which were widely used to remove azo dyes are either inorganic such as activated carbon [3–6], hydrotalcite [7–10], diatomite [11–15] and bentonite [16–19], or organic such as chitosan, alginate, polysaccharide, and polymer materials [20–31] and also hybrid and composite material [32–39]. However, the most challenge for the above adsorbents is the low adsorption capacity and efficiency. Therefore, it is necessary to research and develop new material with good adsorption capacity to treat water contaminated with organic dyes to meet economic efficiency and save costs.

Hydrotalcite (HT) with the general formula is (M²⁺: Mg, Zn, Ca, Fe, Ni…; M³⁺: Al, Cr, Fe…, and Aⁿ⁻: SO₄²⁻, CO₃²⁻, F⁻, Cl⁻, organic anions, or high molecular weight polymers). HTs are interested in using to remove many dyes including MO, amaranth (Am), diamine green B (DGB) and brilliant green (BG), and acid orange (AO) by surface adsorption, interlayer anion exchange, restructuration of calcined HT, and anion exchange [40–42].

Although both polyaniline (Pan) and HT have high adsorption capacity and have been widely used in water treatment. The most important problem is the ability to recover and reuse them. Filtration is an easy method and is widely used but it’s not so effective and fast as using the magnetic field. When combined with a magnetic particle Fe₃O₄, the composite or hybrid from HT will have a magnetic property. As a result, the composite produces a constant suspension in an aqueous solution and is immediately separated from the external environment. On the other hand, modification of hydrotalcite including investigation of magnetic Fe₃O₄/HT nanocomposites (MHT) may have great potential for photocatalysis and environmental remediation [43].

As a conductive polymer, polyaniline (Pan) meets the requirements for environmental treatment applications as both an adsorbent and a photo catalyst according to the following characteristics: high adsorption area, flexible bandgap, and steady−state of activation [44]. Pan nanofiber is an effective adsorbent in studying the removal of methyl orange (MO) and black [45, 46]. Pan is also fabricated as a nanotube and nanoparticle, and they all have high efficiency for removal of MO and crystal violet as well as methylene blue [38, 47–51]. Pan nanoparticles give the highest adsorption capacity due to their high surface area of 1083 m²/g. Besides, it was used as an efficient adsorbent to remove for crystal violet, and methyl orange with the maximum adsorption capacity reaching 245 and 220 mg/g, respectively. In addition, Pan acts as a photo catalyst thanks to its electrical conductivity to increase protonation. Oxidation reactions occur on the catalyst surface, decomposition of the pigment produces intermediate compounds, and the final products are CO₂, SO₄²⁻, NO₃⁻, and NH₄⁺. Therefore, the fast charge generation and slow charge recombination lead to enhanced photo catalytic activity.

In summary, both Pan and MHT have high efficiency in the removal of azo dye. However, studies on the adsorption applications of Pan are limited because Pan has a low surface area resulting in low adsorption efficiency. Therefore, many researches are carried out to composing Pan particles with other materials to enhance the adsorption capacity by various synthesis methods. Another way, many reports have shown that MHT material has been suitable for an adsorbent. So, the combination of Pan and MHT to create a Pan/MHT hybrid or composite material has great potential, and it is still not widely exploited for adsorption, especially in wastewater treatment to adsorp dyes (MO, Congo red, ...).

The structure of the hydroxide porous layer and the ability to exchange ions in MHT combined with Pan will give good capacitive properties and high environmental sustainability, because of the special structure that induces ion exchange, restructuration, and the large surface area, so that Pan/MHT can “trap” the MO dye molecules into its structure, recover MO molecules, and remove them from wastewater. In addition, by the restructuring ability, the Pan/MHT material can be desorped for reuse, easily recovered by magnets, saving costs.

For the above advantages of Pan/MHT composite, in this paper, we synthesized Pan/MHT composite with various mass ratios of . Then, we investigate the adsorption kinetic and isotherm. We also studied the effect of contact time, pH, and adsorbent dose onto the adsorption capacity of MO in water.

2. Experimental Section

2.1. Materials

All the used reagents (Zn(NO₃)₂.4H₂O, Al(NO₃)₃.9H₂O, FeCl₃, FeCl₂, NaOH, HCl, aniline, ammonium persulphate) were analytical grade reagents. Methyl orange (MO) is an azo dye, with the chemical formula C₁₄H₁₅N₃O₃S, and molecular weight is 305.35 g/mol and is often used as an indicator. In this work, MO was used to simulate industrial wastewater in order to evaluate the adsorption capacity of Pan/MHT.

2.2. Preparation of Magnetic Hydrotalcite (MHT)

MHT was preparated by coprecipitation method in the presence of Fe₃O₄ (Figure 1). An accurate amount of 0.1 g Fe₃O₄ was dispersed in distilled water (10 mL). A mixture of Zn(NO₃)₂.4H₂O and Al(NO₃)₃.9H₂O with Zn²⁺/Al³⁺ molar ratio of 2.0 was dissolved in 100 mL distilled water and then coprecipitated into the Fe₃O₄ dispersion. The pH of the reaction solution was kept at around . Then, the coprecipitated mixture was heated for aging at 80°C for 24 hours. The MHT was neutralized with distilled water and dried at 60°C for 6 hours obtain brown MHT powder.

2.3. Preparation of Polyaniline/MHT (Pan/MHT)

Pan/MHTs were fabricated using in situ oxidative polymerization (Figure 2). An accurate amount of 0.2 g MHT was dispersed in a distilled water (40 mL) and alcohol (10 mL) mixture. 0.5 mL of Tween 80 5% was added to the mixture and then sonicated in 30 minutes to acquire a well−dispersed colloidal suspension. The desired amount of aniline dissolved in 25 mL of HCl 0.1 M. The mixture was stirred for 1 hour for complete mixing at 4°C. An accurate amount of APS () was dissolved in the rest of 25 mL HCl and precooled at 4°C for 15 min. APS solution was dropped into the reaction mixture and when completed, the reaction was kept at 4°C with mechanical stirring at 500 rpm. The polymerization was finished after 8 hours, then washed the suspension with a mixture of distilled water:ethanol (70 : 30) for 5 times, and dried in a vacuum dryer at 50°C for 5 hours to obtain a dark green composite Pan/MHT.

2.4. Characterization of the Composite Pan/MHT

The Fourier transform infrared (FT−IR) spectra of Pan, HT, Fe₃O₄, MHT, 0.5 Pan/MHT, 1 Pan/MHT, and 2 Pan/MHT composites were obtained using the KBr method on a Bruker Tensor 27 spectrometer, operated in 400−4000 cm⁻¹ region, at 2 cm⁻¹ resolution, and for 32 scans.

Powder X−ray diffraction patterns of Pan, MHT, 0.5 Pan/MHT, 1 Pan/MHT, and 2 Pan/MHT composites were obtained using a Bruker D8 Advance diffractometer with CuKα radiation (1,5406 Å) at room temperature in the atmospheric pressure. Data were collected in the range of 2 theta from 5 to 70° with a step of 0.02° and a scanning rate of 1°/min.

The structure and morphology of MHT, Pan, and Pan/MHT composites were observed by scanning electron microscopy (SEM). SEM observations were carried out using a Thermo Scientific E−SEM instrument.

The magnetic property of MHT and series of Pan/MHT were analyzed with a vibration sample magneparameter (VSM) method using a Lake Shore Crytotronics device.

The specific surface area and average pore size of Pan/MHT and MHT were determined by nitrogen adsorption t 76 K. The Brunauer−Emmett−Teller (BET) method was employed for the corresponding calculation.

2.5. Batch Studies

The adsorption experiments were performed using the batch equilibrium technique in aqueous solutions at room temperature. Duplicate 20 mg Pan/MHT samples were equilibrated by shaking with 25 mL of MO solution with initial concentrations () ranging between 5 mg/L and 20 mg/L and the effect of pH of MO solution ranging between 3 and 10, and the effect of the adsorbent dose was also studied. The effect of contact time was studied at 15−720 minutes, and the equilibrium was reached at 120 minutes. The MO concentration in the supernatant was measured by a UV − VIS spectrophotometer at a wavelength corresponding to the maximum absorbance for MO (460 nm) and determined using a linear regression equation obtained by plotting a calibration curve for MO over a range of concentrations. All of the adsorptions of MO in batch studies were carried out using a Jasco V630 UV − VIS spectrophotometer.

The adsorption of MO on Pan/MHT could be calculated from the difference between the initial concentration () and the equilibrium one (). The adsorption was expressed in terms of adsorption percentage (%) which was calculated from the following equations:

where and represent the mass of Pan/MHTs and the volume of the suspension, respectively. Here, is the capacity of MO sorption on Pan/MHT after adsorption equilibrium (mg/g).

2.6. Desorption and Reusability of Pan/MHT

For the reusability study, 0.1 g of Pan/MHT was used repeatedly for the adsorption of MO. An adsorption process was performed by adding 0.1 g Pan/MHT in 150 mL of MO at 20 mg/L and shaking for 24 hours to equilibrium adsorption. After that, the Pan/MHT was separated from the MO solution by using a magnetic bar, and the MO solution was analyzed by UV-VIS spectrophotometry to determine the MO adsorption capacity.

The desorption process was performed by dispersing Pan/MHT previously used in the adsorption process in 100 mL of HCl 1.0 M which promotes MO desorption. The desorption was performed in about 1 hour and then separating Pan/MHT by using a magnetic bar. The MO concentration in HCl was also analyzed by UV-VIS spectrophotometry. The cycles of reuse of the same Pan/MHT sample were carried out for a total of 4 cycles. The adsorption capacity of MO and desorption MO concentration was calculated for each cycle of reuse.

3. Results and Discussion

3.1. Characterization of Composite Particles Polyaniline/Mag−HT (MHT)

3.1.1. Fourier Transform IR (FT−IR)

The FT–IR characteristic of MHT as spectrum in Figure 3 shows that a strong absorption band at 1381 cm^–1 is assigned for elongation vibration –NO₃ which is also present for the interlayers of MHT. The weak adsorption at about 1640 cm^–1 is the vibration of –OH in the H₂O structure attached on the interlayer. The wide band at about 3463 cm^–1 is characteristic for elongated vibration of –OH groups from M–OH (Al–OH, Mg–OH, and Fe–OH), lattice, and alternating layer of water: 617, 447, and 409 cm^–1 due to elongated vibration of M–O (Al–O, Zn–O and Fe–O). Thus, Fe₃O₄ has successfully combined with HT material to fabricate MHT hybrid, and the FT −IR spectrum is consistent with that of Sulistyaningsih et al. [52].

The FT–IR infrared spectrum shown in Figure 4 clarifies the nature of the interaction between Pan and MHT in Pan/MHT materials. In the infrared (MIR) region, the peaks between 4000 and 1800 cm^–1 are the prolonged vibration region of the O–H bonds in the hydroxyl group and N–H in the amine group. For MHT, the peak at 3447 cm^–1 is the tensile vibration of –OH that binds the hydroxyl group surface in the structure. The adsorption peaks below 800 cm^–1 at about 786 cm^–1 and 618 cm^–1 are characteristic for M–O bond (Al–O, Zn–O), and the peak at about 429 cm^–1 is assigned for Fe–O.

Pan characterized with the strong absorptions at 3439, 2941, 1569, 1495, 1301, 1130, and 875 cm⁻¹, which was the evidence of the emeraldine form of polyaniline [53–55]. The vibration at about 3220 cm⁻¹ is assigned for protonated radical cation N − H⁺·, and the vibration at about 3443 cm⁻¹ is assigned for the N−H stretching. The characteristic band at 1515 cm⁻¹ was assigned to both C=N and C−N stretching of quinoid ring structure, and the band at 1481 cm⁻¹ was attributed to both C=C and C−N of benzenoid ring structure. All of these absorption peaks were characterized for the inplane bending vibration. The band at around 1301 cm⁻¹ indicated the vibration of the C − N stretching of benzenoid ring, and the one at around 875 cm⁻¹ was the C − H out of plane bending vibration parade-substituted benzene indicating polyaniline polymer formation. In addition, the strong band at 1130 cm⁻¹ was assigned for the C − N=C group attached on the quinoid ring.

3.1.2. X-Ray Diffraction

The XRD of the MHT, Pan, 0.5 Pan/MHT, 1 Pan/MHT, and 2 Pan/MHT are measured in the range of 2θ from 5° to 70°, and the spectrums are shown in Figure 5. The XRD spectrum of MHT from Figure 3(e) has characteristic peaks of HT and some characteristic peaks of Fe₃O₄ at . The characteristic peaks of MHT and HT indicate that both have layered structures with the NO₃⁻ anion in the interlayer. In addition, in MHT material, the 34.6° peak that appeared in HT is divided into two subpeaks. The first peak at a smaller diffraction angle shows the peak of the hydrotalcite, and the second one at a slightly larger diffraction angle shows the magnetite core deposited on the surface of the hydrotalcite corresponding to the magnetite particle combined on the surface of HT. XRD diffraction spectra of MHT material are consistent with that of Sulistyaningsih et al. [52].

The results from the figure show the characteristic diffraction peak of Pan at , , and . Typical diffraction peaks of MHT at , , and . With different from ratios of , there is also different typical diffraction peak of MHT at and . It is because of the bond between Pan and MHT in the material, and the interaction between Pan and MHT can be influenced by hydroxides groups on the MHT surface, affecting the structure and material properties.

3.1.3. SEM Images

The morphology of the material was observed by SEM images in Figure 6. Pan/MHT morphology was observed, in which the distribution of Pan and MHT differed markedly in the proportions. The structural morphology of MHT is a porous material consisting of multilayers, and Pan has the structure of a long carbon chain. The distribution of MHT for Pan is different when changing the mass ratio of Pan. This result is completely consistent with the results of structural analysis by significantly reduced X−ray diffraction.

(a)

(b)

(c)

(d)

(e)

3.1.4. Vibrating Sample Magnetometer (VSM) Analysis

The magnetic properties of MHT and series of Pan/MHT were investigated using a vibrating sample magnetometer at room temperature, and the magnetization curves of MHT and series of Pan/MHT were shown in Figure 7. The roughly coincident hysteresis curves show that the grain size of the MHT metal phase is very small, nanometers in size and is a superparamagnetic material. Because MHT is the hybrid material from HT with only 1 wt% Fe₃O₄ particle, the superparamagnetic characteristic of MHT is the low value of Ms and Mr that are and , and is 20.06 Oe. Pan is a conductive polymer, and it tends to help increasing the ferromagnetic behavior for MHT. However, Pan is diamagnetic, so that when the mass ratio of increased, the values of and decreased as the results in Table 1. And this result is consistent with the announcement of Umare et al. and Jokar et al. [56, 57]. These magnetic properties are high enough that Pan/MHT materials can be separated from the solution by an external magnet.

The low value indicates that the Pan/MHT can be easily separated from the solution by an external magnetic field and redistributed into the solution after the magnetic field is disconnected. This will be an advantage for the separation, recovery, and reuse of the adsorbent as well as the catalyst. MHT has the lowest and which are and . When combined with Pan, the value of composites was decreased, but increasing the mass ratio of helped to decrease the and values. In particularly, the values of 0.5 Pan/MHT, 1 Pan/MHT, and 2 Pan/MHT are , , and , respectively. Then, the values of 0.5 Pan/MHT, 1 Pan/MHT, and 2 Pan/MHT are , , and , respectively.

3.1.5. Bruanauer–Emmett–Teller (BET)

The surface area is well known to be important for adsorption performance. While the pore size of MHT and 2 Pan/MHT is the same which are 26.2 Å and 24.6 Å, the BET surface areas of MHT and 2 Pan/MHT were calculated to be 2.796 m²/g and 15.460 m²/g. The higher surface of 2 Pan/MHT provides more active sites for MO adsorption. This result is consistent with the morphology of MHT and Pan/MHT from the SEM images in Figure 8.

(a)

(b)

3.2. Effect of Contact Time and Kinetic Adsorption

3.2.1. Effect of Contact Time

Figure 9 shows the effect of contact time of 0.5 Pan/MHT, 1 Pan/MHT, and 2 Pan/MHT with 100 mL of 20 mg/L MO solution. The adsorption amounts of MO increased rapidly in the initial 30 minutes for all samples. Then, the adsorption amounts increased slighter in the next 30 minutes. It becomes slow to attained equilibrium time which is 120 minutes for 0.5 Pan/MHT, 1 Pan/MHT, and 240 minutes for 2 Pan/MHT in the same conditions. The difference of equilibrium time for MO adsorption obtained by various adsorbents can be explained by the MO anion adsorption on the adsorbents by surface and anion exchange mechanism. The adsorbent with the higher mass ratio of Pan/MHT, the more MO can be adsorbed. This result is due to the complex adsorption mechanism of Pan such as surface adsorption, anion−exchange, …, which is consistent with the research of Monika et al. and Wang et al. [58, 59].

Kinetic modeling of the adsorption process provides a prediction of adsorption rates and allows the determination of suitable rate expressions characteristic of the possible reaction mechanisms. In this study, the most frequently used models, the pseudofirst−order, the pseudosecond−order, and the intraparticle diffusion model were tested.

Pseudofirst−order kinetics: the linearized from of the pseudofirst−order linearized equation is given as where and (mg/g) are the MO removal at time and at equilibrium. (min⁻¹) is the equilibrium rate constant of the pseudofirst-order equation. The plots of vs. are shown in Figure 10(a), and is predicted can be determined from the slope and intercept of the plot, respectively.

(a)

(b)

(c)

Pseudo−secondorder kinetics: the linearized form of the pseudosecond-order equation is given as where [g/(mg min)] is the equilibrium rate constant of the pseudosecond−order equation. The plot of vs. is shown in Figure 10(b), and and can be determined from the slope and intercept of the plot, respectively.

Intraparticle diffusion model: the intraparticle diffusion model assumes that film diffusion is negligible, and the only rate-controlling step is intraparticle diffusion in the adsorption process [60]. Hence, the adsorbed amount at time should be directly proportional to rather than . The model is given as where is the intraparticle diffusion rate constant (mg/g min^0.5), which can be calculated from the slope of the linear plot of vs. and can be determined from the slope of the plot shown in Figure 10(c).

The kinetic parameters obtained from the application of different models are shown in Table 2. The pseudosecond−order model is the most suitable in describing the adsorption kinetics of MO in all three Pan/MHT composites, based on the correlation coefficient (, 0.998, and 0.999 corresponding to 0.5 Pan/MHT, 1 Pan/MHT, and 2 Pan/MHT), and the experimental and calculated values of are not much different.

3.2.2. Effect of pH on the MO Adsorption

The result from Figure 11 shows that the adsorption efficiency of all three materials decreases gradually according to the pH value of the solution, the efficiency reaches the highest and most stable value at pH from 3 − 4, to pH 5, and the efficiency productivity started to decrease gradually. This is related to the surface area of the material, the presence of hydroxyl groups (OH−) on the surface of the material, and the exchange of protons (H+). This group is both capable of giving and receiving protons according to the pH of the solution when in solid−phase contact. The process of receiving protons on the surface takes place in an acid environment, while proton transfer occurs in an alkaline environment.

3.3. Adsorption Isotherms

3.3.1. Effect of Initial Concentration of MO on Sorption of MO

The effect of initial concentration on MO adsorption onto 0.5 Pan/MHT, 1 Pan/MHT, and 2 Pan/MHT is shown in Figure 12. The experiment was performed with a constant adsorbent dose of 20 mg/25 mL MO. The adsorption capacity of MO increased when increasing the initial MO concentration. The values of 2 Pan/MHT are always higher than ones of 0.5 Pan/MHT and 1 Pan/MHT. This can be due to the structure of 2 Pan/MHT with high surface area as the result analyzed from BET and SEM methods above. For a solid-liquid system, the equilibrium of adsorption is one of the important physic-chemical aspects in the description of adsorption behavior. In this work, the models of Langmuir [61] and Freundlich [62] isotherm are evaluated. The results obtained from the different models provide the behavior of the adsorption mechanisms and the surface properties and affinities of the adsorbent.

The Langmuir isotherm is used to describe the equilibrium between the surface of the solid and the solution and is valid for monolayer adsorption onto a surface with a finite number of identical sites. The Langmuir model equation is given as where (mg/g) is the maximum monolayer adsorption capacity, and (L/mg) is the Langmuir constant related to the binding energy. The plots of vs. are shown in Figure 13(a), and the values of and are calculated from the slope and intercept of the plots, respectively.

(a)

(b)

(c)

The Freundlich isotherm is an empirical equation that assumes that the adsorprion face becomes heterogeneous during the course of the adsorption process. The linearized form of the Freundlich model is given as where (mg/g) and are the Freundlich constants related to adsorption capacity and adsorption intensity, respectively. The plots of log vs. log were shown on Figure 13(b), and the values of and are calculated from the slope and intercept of the plots, respectively.

All the correlation coefficients, values, and the constants calculated from Langmuir and Freundlich models are listed in Table 3. The of both Langmuir and Freundlich models of all three adsorbents is higher than 0.91; so, the adsorption of MO onto Pan/MHT composite appropriate with either monolayer of dyeing molecules covers the Pan/MHT surface or interaction between adsorbents and MO molecules. All three values of the Freundlich model of Pan/MHT composites are higher than of the Langmuir model. In particularly, corresponding to 0.5 Pan/MHT, 1 Pan/MHT, and 2 Pan/MHT. In addition, the values of three composites are higher than 2 ( for 0.5 Pan/MHT, 1 Pan/MHT, and 2 Pan/MHT, respectively) which indicates that the MO adsorption on Pan/MHT composite is not only monolayer surface adsorption. The mechanism of MO adsorption onto Pan/MHT composite is either of the surface adsorption or other types of interactions, such as electrostatic interaction, ion exchange, hydrogen bonding, and van der Waals forces. In all three composites, 2 Pan/MHT is the most suitable for the Freundlich model and the Langmuir model too. The MO adsorption capacity of 2 Pan/MHT is also the highest with .

Dubinin-Radushkevich (D-R) isotherm is generally used to describe the sorption isotherms of a single solute system (Figure 13(c)). The D-R isotherm can also help to confirm that the adsorption process was chemisorption or physical adsorption [63]. D-R equation is represented as follows: where is equilibrium adsorbent-phase concentration of adsorbate (mg/g), and is theoretical saturation capacity (mg/g). The plots of ε² vs. ln were shown in Figure 10(c), and the values of β and are calculated from the slope and intercept of the plots, respectively. β is the activity coefficient related to the mean free energy of adsorption (mol²/kJ²), and ε is the polanyipotential (kJ/mol). where is the universal gas constant (8.314 J/mol.K), is the Kelvin temperature (K), and is the equilibrium aqueous phase concentration of adsorbate (mg/L).

The D-R model is mainly used to estimate the average free energy of adsorption (kJ/mol) when , the adsorption is physical adsorption and when , the adsorption is chemisorption [64]. The adsorption energy values () of 0.5 Pan/MHT, 1 Pan/MHT, and 2 Pan/MHT are under 8 kJ/mol. In particularly, corresponding to 0.5 Pan/MHT, 1 Pan/MHT, and 2 Pan/MHT. This result indicates that the adsorption process of MO on three kinds of Pan/MHT composites is physical adsorption.

3.3.2. Effect of 2 Pan/MHT Dosage on the Sorption of MO

The result from Figure 14 shows the adsorption efficiency (H %) when using a different dose of 2 Pan/MHT (0.01, 0.02, and 0.03 g) and shows the adsorption efficiency increases when increasing 2 Pan/MHT dose.

For all 3 doses of 2 Pan/MHT, MO was immediately adsorbed on 2 Pan/MHT and after 30 minutes, the adsorption efficiency obtained 55.39%, 63.88%, and 65.97% according to use of 0.01, 0.02, and 0.03 g of 2 Pan/MHT, respectively. Then, the adsorption efficiency increase slightly and reached to equilibrium after 240 minutes with the adsorption efficiency obtained 64.43%, 68.59%, and 77.37% according to the use of 0.01, 0.02, and 0.03 g of 2 Pan/MHT, respectively. This result is expected because the increase of adsorbent dose leads to a greater surface area.

The FT–IR spectra of MO, 2 Pan/MHT, and 2 Pan/MHT after adsorption of MO are shown in Figure 15(a). MO is characterized by the peak at 2896 cm^-1 for asymmetric CH₃ stretching vibration; the peaks at 1520 cm^-1 and 1421 cm^-1 are assigned for C=C–H in plane CH bend; peak at 817 cm^-1 is characteristic of the benzene ring. The peak at 1608.32 cm^-1 is assigned for –N=N–, and the peaks at 1201 cm^-1 and 1121 cm^-1 are assigned for –C–N. The peaks at 697 cm^-1, 623 cm^-1, and 574 cm^-1 are assigned for the stretching vibration -C-S-, and the peak at 1367 cm^-1 is assigned for the stretching vibration S=O. These characteristics also exist on Pan/MHT materials after adsorption, demonstrating the presence of MO dye on the material, and this result is consistent with the announcement of Harikumar et al. [65].

(a)

(b)

(c)

SEM images of 2 Pan/MHT and 2 Pan/MHT after adsorption of MO (Figures 15(b) and 15(c)) clearly show the material surface before and after MO adsorption. The surface and pores of 2 Pan/MHT after adsorption of MO are covered with the MO (adsorbed components), and the result is the surface of the material more homogeneous than the original. It is mean that the material samples after adsorption have almost filled gaps.

3.4. Desorption of MO and Reusability of Pan/MHT

Another parameter that defines the functionality of adsorbent material is its capacity to be regenerated and reused in several adsorption and desorption cycles. For this reason, MO adsorption and desorption experiments were performed with Pan/MHT by using a 0.1 M HCl solution as an eluent. This eluent was chosen because in acid conditions, Pan is in emeraldine salt and is doped with H+ ions, and MO is in its cationic form [66, 67]. Therefore, due to electrostatic repulsions, the MO molecules would be desorbed from the composite structure.

Figure 16 shows the adsorption and desorption efficiency of MO after 4 cycles. The result show that the MO adsorption decreases to 12.86%, 14.28%, and 9.16% according to using 0.5 Pan/MHT, 1 Pan/MHT, and 2 Pan/MHT. The MO desorption from 0.5 Pan/MHT, 1 Pan/MHT, and 2 Pan/MHT also decreases to 21.51%, 19.7%, and 13.57%, respectively. This can be due to the increase of Pan in a composite structure, which enhances both adsorption and desorption of MO on the adsorbent. Thus, Pan/MHT surface can be regenerated without a problem. Although MO is completely desorbed, the adsorption percentage decreases, and this behavior is because of the loss of Pan due to stirring and material management. Therefore, this material can be reused in multiple cycles if it wants to be coupled to a recirculation system.

(a)

(b)

(c)

(d)

The results show that at a low pH 3 − 4, the MO adsorption capacity (H %) obtained over 80% after 3 cycles of reuse. When the solution , the MO adsorption decreased and obtained 60− 73% efficiency of MO removal after 3 cycles of reuse. This shows that the MO adsorption and desorption are suitable for performance in acidic environments at pH 3 − 4.

3.5. Mechanism of Adsorption

With all the results above, the process of adsorption, recovery, and desorption of MO on Pan/MHT was described as Figure 17(a). The adsorption and desorption mechanism of MO on Pan/MHT are the combination of chemisorption and physical adsorption, which can be illustrated in Figures 17(b)–17(d) and explained as below: (i)In solution, MO molecule is dissociated into M-SO3^- with M is an organic part of dyeing molecule. Pan is a conducting polymer with NH⁺ group on full backbone that will interact with M-SO3^-. The electrostatic interactions are preferably involved in MO adsorption onto Pan particles. Besides, the adsorption experiment studied on Pan/MHT was found to have followed the pseudosecond-order model which indicates the chemisorption mechanism of Pan/MHT(ii)The presence of MHT gives the good adsorption of MO because of the anion exchangeable. For this mechanism, the anion associated with the interlayer Pan/MHT is exchanged with MO anionic molecules in solution. It also means that the MO anion will be trapped into the interlayer structure, and it indicates the physical adsorption mechanical of Pan/MHT

(a)

(b)

(c)

(d)

4. Conclusion

The MHT material has been synthesized with 0.1 g Fe₃O₄ added during the coprecipitation process with the Zn²⁺/Al³⁺ salt mixture to create a magnetic MHT material. Then, a series of Pan/MHT composites were successfully synthesized with different mass ratios of . All Pan/MHT composites were characterized by analyzing methods of SEM, FT−IR, XRD, BET, and VSM and then studying for MO adsorption. The key findings of this research are (i)2 Pan/MHT was the best material with high surface area (15.46 m²/g), high Hc (18.56 Oe), and low Ms () and Mr ()(ii)According to the MO adsorption kinetic studies, all of 0.5 Pan/MHT, 1 Pan/MHT, and 2 Pan/MHT composites are suitable with pseudosecond−order model, based on the correlation coefficient ( corresponding to 0.5 Pan/MHT, 1 Pan/MHT, and 2 Pan/MHT), and the experimental and calculated values of are not much different. 2 Pan/MHT had the highest adsorption capacity in studying the effect of time contact and pH of MO solution(iii)The of both Langmuir and Freundlich models of all three adsorbents is higher than 0.91; so, the adsorption of MO onto Pan/MHT composite appropriate with either monolayer of dyeing molecules covers the Pan/MHT surface or interaction between adsorbents and MO molecules(iv)The adsorption energy of all 0.5 Pan/MHT, 1 Pan/MHT, and 2 Pan/MHT is 0.273, 0.277, and 0.269 kJ/mol, and all of them are below 8 kJ/mol. This result indicates that the adsorption process of MO on three kinds of Pan/MHT composites is physical adsorption(v)Pan/MHT was also investigated to reuse after desorption of MO in 0.1 M HCl, and the result shows that 2 Pan/MHT can be reused for 4 cycles with (vi)The mechanism of MO adsorption onto Pan/MHT composite is either of the surface adsorption or other types of interactions, such as electrostatic interaction, ion exchange, hydrogen bonding, and van der Waals forces

Data Availability

The data used to support the findings of this study are available from the corresponding author upon request.

Conflicts of Interest

The authors declare that there is no conflict of interest regarding the publication of this paper.

Acknowledgments

This work was supported by Kurita Water and Environment Foundation (KWEF) for the award of KURITA Overseas Research Grant 2020 under Grant [20Pvn032-K43]. The authors thank to Institute of Chemical Technology for their warmly analysis equipment support.

References

Y. el maguana, N. Elhadiri, M. Bouchdoug, M. Benchanaa, and A. Boussetta, “Optimization of preparation conditions of novel adsorbent from sugar scum using response surface methodology for removal of methylene blue,” Journal of Chemistry, vol. 2018, Article ID 2093654, 10 pages, 2018.
View at: Publisher Site | Google Scholar
R. Kant, “Adsorption of dye eosin from an aqueous solution on two different samples of activated carbon by static batch method,” Journal of Water Resource and Protection, vol. 4, no. 2, pp. 93–98, 2012.
View at: Publisher Site | Google Scholar
U. Maheshwari, D. Deshpande, K. Zare, and P. Vardhe, “Removal of Dye from Aqueous Solution by Using Activated Carbon,” Research Journal of Engineering Science, vol. 6, no. 7, 2017.
View at: Google Scholar
P. K. Malik, “Dye removal from wastewater using activated carbon developed from sawdust: adsorption equilibrium and kinetics,” Journal of Hazardous Materials, vol. 113, no. 1–3, pp. 81–88, 2004.
View at: Publisher Site | Google Scholar
H. O. Soonmi, “Removal of dye by adsorption onto activated carbons: review,” Eurasian Journal of Analytical Chemistry, vol. 13, no. 4, pp. 332–338, 2018.
View at: Google Scholar
A. A. Attia, W. E. Rashwan, and S. A. Khedr, “Capacity of activated carbon in the removal of acid dyes subsequent to its thermal treatment,” Dyes and Pigments, vol. 69, no. 3, pp. 128–136, 2006.
View at: Publisher Site | Google Scholar
E. Heraldy, S. Santosa, T. Triyono, and K. Wijaya, “Anionic and Cationic Dyes Removal from Aqueous Solutions by Adsorption onto Synthetic Mg/Al Hydrotalcite-Like Compound,” Indonesian Journal of Chemistry, vol. 15, no. 3, pp. 234–241, 2015.
View at: Publisher Site | Google Scholar
N. Lazaridis, T. D. Karapantsios, and D. Georgantas, “Kinetic analysis for the removal of a reactive dye from aqueous solution onto hydrotalcite by adsorption,” Water Research, vol. 37, no. 12, pp. 3023–3033, 2003.
View at: Publisher Site | Google Scholar
A. El Khanchaoui, M. Sajieddine, M. Mansori, and A. Essoumhi, “Anionic dye adsorption on ZnAl hydrotalcite-type and regeneration studies based on “memory effect”,” International Journal of Environmental Analytical Chemistry, pp. 1–19, 2020.
View at: Publisher Site | Google Scholar
V. T. Lam, T.-U. T. Dao, H.-T. T. Nguyen et al., “Process optimization studies of Congo red dye adsorption onto magnesium aluminium layered double hydroxide using response surface methodology,” Polish Journal of Environmental Studies, vol. 30, no. 1, pp. 679–687, 2021.
View at: Publisher Site | Google Scholar
E. Erdem, G. Cölgeçen, and R. Donat, “The removal of textile dyes by diatomite earth,” Journal of Colloid and Interface Science, vol. 282, no. 2, pp. 314–319, 2005.
View at: Publisher Site | Google Scholar
K. Xia, X. Liu, Z. Chen, L. Fang, H. Du, and X. Zhang, “Efficient and sustainable treatment of anionic dye wastewaters using porous cationic diatomite,” Journal of the Taiwan Institute of Chemical Engineers, vol. 113, pp. 8–15, 2020.
View at: Publisher Site | Google Scholar
B. H. Dang Son, V. Quang Mai, D. Xuan du, N. Hai Phong, and D. Quang Khieu, “A study on astrazon black AFDL dye adsorption onto Vietnamese diatomite,” Journal of Chemistry, vol. 2016, Article ID 8685437, 11 pages, 2016.
View at: Publisher Site | Google Scholar
R. Zheng, H. Gao, J. Guan, Z. Ren, and J. Tian, “Characteristics of cationic red X-GRL adsorption by diatomite tailings,” Journal of Wuhan University of Technology-Mater. Sci. Ed., vol. 32, no. 5, pp. 1038–1047, 2017.
View at: Publisher Site | Google Scholar
Y.-H. Zhao, J.-T. Geng, J.-C. Cai, Y.-F. Cai, and C.-Y. Cao, “Adsorption performance of basic fuchsin on alkali-activated diatomite,” Adsorption Science & Technology, vol. 38, no. 5–6, pp. 151–167, 2020.
View at: Publisher Site | Google Scholar
B. Guezzen, M. Adjdir, B. Medjahed, M. A. Didi, and P. G. Weidler, “Kinetic study and box–Behnken design approach to optimize the sorption process of toxic azo dye onto organo-modified bentonite,” Canadian Journal of Chemistry, vol. 98, no. 5, pp. 215–221, 2020.
View at: Publisher Site | Google Scholar
A. Berez, F. Ayari, N. Abidi, G. Schäfer, and M. Trabelsi-Ayadi, “Adsorption-desorption processes of azo dye on natural bentonite: batch experiments and modelling,” Clay Minerals, vol. 49, no. 5, pp. 747–763, 2014.
View at: Publisher Site | Google Scholar
H. Zhang, J. Zhou, Y. Muhammad et al., “Citric acid modified bentonite for Congo red adsorption,” Frontiers in Materials, vol. 6, p. 5, 2019.
View at: Publisher Site | Google Scholar
S. A. S. Aldbouni, E. A. S. Alhyali, and A. A. H. Alkazraji, “Equilibrium and thermodynamic studys of adsorption of azo dyes on the local bentonite clay,” Journal of Education and Science, vol. 28, no. 2, pp. 50–70, 2019.
View at: Publisher Site | Google Scholar
P. Semeraro, “Removal of an azo textile dye from wastewater by cyclodextrin-epichlorohydrin polymers,” in Cyclodextrin - A Versatile Ingredient, Ch. 13, J. A. Gabaldón, Ed., IntechOpen, Rijeka, 2018.
View at: Publisher Site | Google Scholar
G. Bayramoglu and M. Y. Arica, “Grafting of regenerated cellulose films with fibrous polymer and modified into phosphate and sulfate groups: application for removal of a model azo-dye,” Colloids and Surfaces A: Physicochemical and Engineering Aspects, vol. 614, article 126173, 2021.
View at: Publisher Site | Google Scholar
S. Zeng, J. Tan, X. Xu, X. Huang, and L. Zhou, “Facile synthesis of amphiphilic peach gum polysaccharide as a robust host for efficient encapsulation of methylene blue and methyl orange dyes from water,” International Journal of Biological Macromolecules, vol. 154, pp. 974–980, 2020.
View at: Publisher Site | Google Scholar
Y. Song, J. Tan, G. Wang, and L. Zhou, “Superior amine-rich gel adsorbent from peach gum polysaccharide for highly efficient removal of anionic dyes,” Carbohydrate Polymers, vol. 199, pp. 178–185, 2018.
View at: Publisher Site | Google Scholar
H. Gao, S. Zhao, X. Cheng, X. Wang, and L. Zheng, “Removal of anionic azo dyes from aqueous solution using magnetic polymer multi-wall carbon nanotube nanocomposite as adsorbent,” Chemical Engineering Journal, vol. 223, pp. 84–90, 2013.
View at: Publisher Site | Google Scholar
X. Meng, B. Scheidemantle, M. Li et al., “Synthesis, characterization, and utilization of a lignin-based adsorbent for effective removal of azo dye from aqueous solution,” ACS Omega, vol. 5, no. 6, pp. 2865–2877, 2020.
View at: Publisher Site | Google Scholar
R. C. da Silva, S. B. de Aguiar, P. L. R. da Cunha, R. C. M. de Paula, and J. P. A. Feitosa, “Effect of microwave on the synthesis of polyacrylamide-g-chitosan gel for azo dye removal,” Reactive and Functional Polymers, vol. 148, article 104491, 2020.
View at: Publisher Site | Google Scholar
Y. Yildirim, H. Yilmaz, G. Ak, and S. Sanlier, “New copolymer of acrylamide with allyl methacrylate and its capacity for the removal of azo dyes,” Polímeros, vol. 25, no. 2, pp. 137–145, 2015.
View at: Publisher Site | Google Scholar
M. Ait Himi, S. El Ghachtouli, A. Amarray, Z. Zaroual, P. Bonnaillie, and M. Azzi, “Removal of azo dye calcon using polyaniline films electrodeposited on SnO2 substrate,” Physical Chemistry Research, vol. 8, no. 1, pp. 111–124, 2020.
View at: Publisher Site | Google Scholar
R. S. Aliabadi and N. O. Mahmoodi, “Synthesis and characterization of polypyrrole, polyaniline nanoparticles and their nanocomposite for removal of azo dyes; sunset yellow and Congo red,” Journal of Cleaner Production, vol. 179, pp. 235–245, 2018.
View at: Publisher Site | Google Scholar
K. Ghosh, N. Bar, A. B. Biswas, and S. K. Das, “Removal of methylene blue (Aq) using untreated and acid-treated eucalyptus leaves and GA-ANN modelling,” The Canadian Journal of Chemical Engineering, vol. 97, no. 11, pp. 2883–2898, 2019.
View at: Publisher Site | Google Scholar
I. Ghosh, S. Kar, T. Chatterjee, N. Bar, and S. Das, “Removal of methylene blue from aqueous solution using _Lathyrus sativus_ husk: adsorption study, MPR and ANN modelling,” Process Safety and Environmental Protection, vol. 149, pp. 345–361, 2021.
View at: Publisher Site | Google Scholar
T. Posati, A. Listwan, G. Sotgiu, A. Torreggiani, R. Zamboni, and A. Aluigi, “Keratin/hydrotalcites hybrid sponges as promising adsorbents for cationic and anionic dyes,” Frontiers in Bioengineering and Biotechnology, vol. 8, p. 68, 2020.
View at: Publisher Site | Google Scholar
L. Zheng, C. Wang, Y. Shu, X. Yan, and L. Li, “Utilization of diatomite/chitosan-Fe (III) composite for the removal of anionic azo dyes from wastewater: equilibrium, kinetics and thermodynamics,” Colloids and Surfaces A: Physicochemical and Engineering Aspects, vol. 468, pp. 129–139, 2015.
View at: Publisher Site | Google Scholar
Y. Z. Zhang, J. Li, W. J. Li, and Y. Li, “Adsorption of sunset yellow FCF from aqueous solution by chitosan-modified diatomite,” Water Science and Technology, vol. 72, no. 10, pp. 1861–1868, 2015.
View at: Publisher Site | Google Scholar
X.-J. Wu, J.-D. Wang, and L.-Q. Cao, “Characterization and Adsorption Performance of Chitosan/Diatomite Membranes for Orange G Removal,” e-Polymers, vol. 16, no. 2, pp. 99–109, 2016.
View at: Publisher Site | Google Scholar
A. A. Khodabandelou, R. Darvishi Cheshmeh Soltani, H. Gudini, M. J. Tarrahi, and F. Fazelinia, “Removal of azo dye from synthetic wastewater using immobilized nano-diatomite within calcium alginate TT - حذف رنگ آزو از فاضلاب مصنوعی با استفاده ازنانو-دیاتومیت تثبیت شده در آلژینات کلسیم,” SSUJ, vol. 14, no. 6, pp. 17–35, 2016.
View at: Google Scholar
Q. Liu, B. Yang, L. Zhang, and R. Huang, “Adsorption of an anionic azo dye by cross-linked chitosan/bentonite composite,” International Journal of Biological Macromolecules, vol. 72, pp. 1129–1135, 2015.
View at: Publisher Site | Google Scholar
J. Tie, X. Fang, X. Wang et al., “Adsorptive removal of a reactive azo dye using polyaniline-intercalated bentonite,” Polish Journal of Environmental Studies, vol. 26, no. 3, pp. 1259–1268, 2017.
View at: Publisher Site | Google Scholar
A. Sienkiewicz, A. Kierys, and J. Goworek, “Polymer-hybrid silica composite for the azo dye removal from aqueous solution,” Journal of Dispersion Science and Technology, vol. 40, no. 10, pp. 1396–1404, 2019.
View at: Publisher Site | Google Scholar
K. Abdellaoui, I. Pavlovic, and C. Barriga, “Nanohybrid layered double hydroxides used to remove several dyes from water,” ChemEngineering, vol. 3, no. 2, p. 41, 2019.
View at: Publisher Site | Google Scholar
H. Zaghouane-Boudiaf, M. Boutahala, and L. Arab, “Removal of methyl orange from aqueous solution by uncalcined and calcined MgNiAl layered double hydroxides (LDHs),” Chemical Engineering Journal, vol. 187, pp. 142–149, 2012.
View at: Publisher Site | Google Scholar
R. Extremera, I. Pavlovic, M. R. Pérez, and C. Barriga, “Removal of acid orange 10 by calcined mg/Al layered double hydroxides from water and recovery of the adsorbed dye,” Chemical Engineering Journal, vol. 213, pp. 392–400, 2012.
View at: Publisher Site | Google Scholar
C. Prasad, H. Tang, and W. Liu, “Magnetic Fe3O4 based layered double hydroxides (LDHs) nanocomposites (Fe3O4/LDHs): recent review of progress in synthesis, properties and applications,” Journal of Nanostructure in Chemistry, vol. 8, no. 4, pp. 393–412, 2018.
View at: Publisher Site | Google Scholar
M. Duhan and R. Kaur, “Adsorptive removal of methyl Orange with polyaniline nanofibers: an unconventional adsorbent for water treatment,” Environmental Technology, vol. 41, no. 23, pp. 2977–2990, 2020.
View at: Publisher Site | Google Scholar
M. Tanzifi, M. Tavakkoli Yaraki, M. Karami et al., “Modelling of dye adsorption from aqueous solution on polyaniline/carboxymethyl cellulose/TiO₂ nanocomposites,” Journal of Colloid and Interface Science, vol. 519, pp. 154–173, 2018.
View at: Publisher Site | Google Scholar
M. Bhaumik, R. I. McCrindle, A. Maity, S. Agarwal, and V. Gupta, “Polyaniline nanofibers as highly effective re-usable adsorbent for removal of reactive black 5 from aqueous solutions,” Journal of Colloid and Interface Science, vol. 466, pp. 442–451, 2016.
View at: Publisher Site | Google Scholar
M. Saad, H. Tahir, J. Khan, U. Hameed, and A. Saud, “Synthesis of polyaniline nanoparticles and their application for the removal of crystal violet dye by ultrasonicated adsorption process based on response surface methodology,” Ultrasonics Sonochemistry, vol. 34, pp. 600–608, 2017.
View at: Publisher Site | Google Scholar
A. Muhammad, A.-H. Shah, and S. Bilal, “Comparative study of the adsorption of acid blue 40 on polyaniline, magnetic oxide and their composites: synthesis, characterization and application,” Materials, vol. 12, no. 18, p. 2854, 2019.
View at: Publisher Site | Google Scholar
M. Ayad and A. A. el-Nasr, “Adsorption of cationic dye (methylene blue) from water using polyaniline nanotubes base,” The Journal of Physical Chemistry C, vol. 114, no. 34, pp. 14377–14383, 2010.
View at: Publisher Site | Google Scholar
M. Ayad and A. A. el-Nasr, “Anionic dye (acid green 25) adsorption from water by using polyaniline nanotubes salt/silica composite,” Journal of Nanostructure in Chemistry, vol. 3, no. 1, 2012.
View at: Publisher Site | Google Scholar
V. Sharma, P. Rekha, and P. Mohanty, “Nanoporous hypercrosslinked polyaniline: an efficient adsorbent for the adsorptive removal of cationic and anionic dyes,” Journal of Molecular Liquid, vol. 222, pp. 1091–1100, 2016.
View at: Publisher Site | Google Scholar
T. Sulistyaningsih, S. J. Santosa, D. Siswanta, and B. Rusdiarso, “Preparation of magnetite-mg/Al hydrotalcite through hydrothermal process and subsequent calcination,” Advanced Materials Research, vol. 1101, pp. 336–339, 2015.
View at: Publisher Site | Google Scholar
K. Zhu, Y. Gao, X. Tan, and C. Chen, “Polyaniline modified mg/Al layered double hydroxide composites and their application in efficient removal of Cr (VI),” ACS Sustainable Chemistry & Engineering, vol. 4, no. 8, pp. 4361–4369, 2016.
View at: Publisher Site | Google Scholar
X. Wu, X. Tan, S. Yang et al., “Coexistence of adsorption and coagulation processes of both arsenate and NOM from contaminated groundwater by nanocrystallined mg/Al layered double hydroxides,” Water Research, vol. 47, no. 12, pp. 4159–4168, 2013.
View at: Publisher Site | Google Scholar
T. Wen, Q. Fan, X. Tan et al., “A Core-shell structure of polyaniline coated protonic titanate nanobelt composites for both Cr(VI) and humic acid removal,” Polymer Chemistry, vol. 7, no. 4, pp. 785–794, 2016.
View at: Publisher Site | Google Scholar
S. S. Umare, B. H. Shambharkar, and R. S. Ningthoujam, “Synthesis and characterization of polyaniline- Fe₃O₄ nanocomposite: electrical conductivity, magnetic, electrochemical studies,” Synthetic Metals, vol. 160, no. 17-18, pp. 1815–1821, 2010.
View at: Publisher Site | Google Scholar
M. Jokar, R. Foroutani, M. Safaralizadeh, and K. Farhadi, “Synthesis and characterization of polyaniline/Fe₃O₄ magnetic nanocomposite as practical approach for fluoride removal process,” Annual Research & Review in Biology, vol. 4, no. 21, pp. 3262–3273, 2014.
View at: Publisher Site | Google Scholar
M. Duhan and R. Kaur, “Nano-structured polyaniline as a potential adsorbent for methylene blue dye removal from effluent,” Journal of Composites Science, vol. 5, no. 1, p. 7, 2021.
View at: Publisher Site | Google Scholar
N. Wang, J. Chen, J. Wang, J. Feng, and W. Yan, “Removal of methylene blue by polyaniline/TiO₂ hydrate: adsorption kinetic, isotherm and mechanism studies,” Powder Technology, vol. 347, pp. 93–102, 2019.
View at: Publisher Site | Google Scholar
A. I. Okoye, P. M. Ejikeme, and O. D. Onukwuli, “Lead removal from wastewater using fluted pumpkin seed Shell activated carbon: adsorption modeling and kinetics,” International Journal of Environmental Science & Technology, vol. 7, no. 4, pp. 793–800, 2010.
View at: Publisher Site | Google Scholar
I. Langmuir, “The constitution and fundamental properties of solids and liquids. PART I. SOLIDS,” Journal of the American Chemical Society, vol. 38, no. 11, pp. 2221–2295, 1916.
View at: Publisher Site | Google Scholar
H. Freundlich, “Über Die Adsorption in Lösungen,” Zeitschrift für Physikalische Chemie, vol. 57U, no. 1, pp. 385–470, 1907.
View at: Publisher Site | Google Scholar
M. Dubinin, “The equation of the characteristic curve of activated charcoal,” Proceedings of the USSR Academy of Sciences, vol. 55, pp. 327–329, 1947.
View at: Google Scholar
A. Günay, E. Arslankaya, and I. Tosun, “Lead removal from aqueous solution by natural and pretreated clinoptilolite: adsorption equilibrium and kinetics,” Journal of Hazardous Materials, vol. 146, no. 1–2, pp. 362–371, 2007.
View at: Publisher Site | Google Scholar
H. PS, L. Joseph, and D. A, “Photocatalytic degradation of textile dyes by hydrogel supported titanium dioxide nanoparticles,” Journal of Environmental Engineering and Ecological Science, vol. 2, no. 1, p. 2, 2013.
View at: Publisher Site | Google Scholar
K. Haitham, S. Razak, and M. A. Nawi, “Kinetics and isotherm studies of methyl orange adsorption by a highly recyclable immobilized polyaniline on a glass plate,” Arabian Journal of Chemistry, vol. 12, no. 7, pp. 1595–1606, 2019.
View at: Publisher Site | Google Scholar
L. S. Mendieta-Rodríguez, L. M. González-Rodríguez, J. J. Alcaraz-Espinoza, A. E. Chávez-Guajardo, and J. C. Medina-Llamas, “Synthesis and characterization of a polyurethane-polyaniline macroporous foam material for methyl orange removal in aqueous media,” Materials Today Communications, vol. 26, article 102155, 2021.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2021 Thi Tuong An Tran et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Adsorption Science & Technology

Preparation of Magnetic Composite Polyaniline/Fe3O4−Hydrotalcite and Performance in Removal of Methyl Orange

Abstract

1. Introduction

2. Experimental Section

2.1. Materials

2.2. Preparation of Magnetic Hydrotalcite (MHT)

2.3. Preparation of Polyaniline/MHT (Pan/MHT)

2.4. Characterization of the Composite Pan/MHT

2.5. Batch Studies

2.6. Desorption and Reusability of Pan/MHT

3. Results and Discussion

3.1. Characterization of Composite Particles Polyaniline/Mag−HT (MHT)

3.1.1. Fourier Transform IR (FT−IR)

3.1.2. X-Ray Diffraction

3.1.3. SEM Images

3.1.4. Vibrating Sample Magnetometer (VSM) Analysis

3.1.5. Bruanauer–Emmett–Teller (BET)

3.2. Effect of Contact Time and Kinetic Adsorption

3.2.1. Effect of Contact Time

3.2.2. Effect of pH on the MO Adsorption

3.3. Adsorption Isotherms

3.3.1. Effect of Initial Concentration of MO on Sorption of MO

3.3.2. Effect of 2 Pan/MHT Dosage on the Sorption of MO

3.4. Desorption of MO and Reusability of Pan/MHT

3.5. Mechanism of Adsorption

4. Conclusion

Data Availability

Conflicts of Interest

Acknowledgments

References

Copyright

Preparation of Magnetic Composite Polyaniline/Fe₃O₄−Hydrotalcite and Performance in Removal of Methyl Orange