Flexural Strength of Translucent Zirconia Materials Produced with Different Multilayer Technologies: An In Vitro Study

Bakitian, Fahad

doi:https://doi.org/10.1155/2024/8410101

International Journal of Dentistry

On this page

Abstract Introduction Results Discussion Conclusion Data Availability Conflicts of Interest Acknowledgments References Copyright Related Articles

Research Article | Open Access

Volume 2024 | Article ID 8410101 | https://doi.org/10.1155/2024/8410101

Flexural Strength of Translucent Zirconia Materials Produced with Different Multilayer Technologies: An In Vitro Study

Fahad Bakitian¹

Academic Editor: Gaetano Paolone

Received24 Jan 2024

Revised08 Mar 2024

Accepted10 Mar 2024

Published27 Mar 2024

Abstract

Objective. To evaluate the flexural strength of two translucent multilayered zirconia materials produced with different multilayer technologies. Methodology. Eighty bar-shaped zirconia specimens were prepared from two different multilayered zirconia materials (IPS e.max® ZirCAD Prime and KATANA™ Multilayered Zirconia HTML) and divided into eight groups (n = 10) based on the materials used and the individual layers of the disc for each material: Dentin Prime, Transition Prime, Translucent Prime, Multilayered Prime, Dentin HTML, Transition HTML, Translucent HTML, and Multilayered HTML. The bar-shaped zirconia specimens were cut to include all the layers from translucent to dentin In Multilayered Prime and Multilayered HTML groups. All specimens were fully sintered after cutting from multilayered zirconia discs and subjected to three-point flexural strength test using the universal testing machine. Results. The specimens made of HTML zirconia material showed significantly () higher flexural strength than those made of IPS e.max® ZirCAD Prime material, with no significant difference () compared to the specimens in the Dentin Prime group. The Dentin Prime specimens had the highest flexural strength (743 ± 116 MPa) compared to those in the Translucent Prime (514 ± 120 MPa), Transition Prime (575 ± 102 MPa), and Multilayered Prime (531 ± 132 MPa) groups. The flexural strength of the specimens from the individual layers of HTML zirconia material was not significantly different () among the Dentin HTML (763 ± 56 MPa), Translucent HTML (791 ± 106 MPa), Transition HTML (816 ± 85 MPa), and Multilayered HTML (793 ± 102 MPa) groups. Conclusion. Multilayered zirconia materials produced with different yttria contents by layer have lower flexural strength than those produced with gradient shade technology and the same yttria content for each layer. Therefore, various factors such as the type of prostheses, nesting strategies of prostheses within the zirconia disc, and the desired aesthetical requirements should be considered when selecting the multilayered zirconia materials.

1. Introduction

Tetragonal zirconia polycrystal stabilized with 3 mol% yttria (3Y-TZP) has been among the most used dental ceramic materials since the nineties [1]. It is a reliable restorative material for making fixed dental prostheses (FDPs) with higher strength and toughness properties compared to other dental ceramic materials [2, 3]. However, due to its high opacity, early-generation zirconia material was specifically used as a framework for FDPs and veneered with aesthetical materials [4]. The inferior optical properties of this zircona material have been attributed to the presence of tetragonal crystal phase [1, 4]. Although tetragonal crystals contribute to material fracture toughness through the phase transformation toughening mechanism, they are birefringent and reduce translucency due to refraction and reflection of light at grain boundaries [4–6]. Conversely, the cubic crystal phase offers improved translucency due to the isotropic properties, which makes the refractive index unaffected by the direction of light travel [7–9]. Nonetheless, zirconia material with a substantial amount of cubic crystals would benefit less from the phase transformation toughening, making it less resistant to fracture [7–9].

Recently, new zirconia materials have been developed with enhanced translucent properties, allowing full-contour (monolithic) FDPs to overcome the clinical issues of veneer chipping and fracture [10, 11]. The improved translucency was achieved by altering the chemical composition by using a higher yttria content compared to the traditional zirconia, which results in more of the optically isotropic cubic phase [7–9]. Nevertheless, such attempts to raise the translucency of zirconia materials can result in inferior mechanical properties in terms of fracture strength and toughness [7–9]. To overcome this issue, manufacturers have developed new multilayered zirconia materials intended for monolithic FDPs.

Translucent multilayered zirconia products are different from each other based on the implemented multilayer technology, with some products having the same chemical composition by layer but with a gradient shade technology [12, 13]. In this technology, zirconia materials have different color additives by layer to gradually increase the translucency from the cervical area to the incisal area of the restoration. The multilayering effect is achieved by controlling the color additives in each layer, and the differences in translucency are achieved indirectly by reducing light transmittance. The translucent layer is free of color pigments, while the opaque layer has the highest saturation of color pigments. It is important to note that achieving a balance between mechanical and optical properties in multilayered zirconia materials using grade shade technology can be challenging. This balance is highly dependent on the yttria content in the material [7]. For instance, while multilayered zirconia with 3% mol yttria content produced with grade shade technology has high strength, its translucency may be low. Conversely, using the same technology, multilayered zirconia with 4% or 5% mol yttria contents may have high translucency but limited flexural strength [8, 9].

To address this issue, other multilayered zirconia materials have been developed featuring different chemical compositions in terms of yttria contents in each layer, resulting in a material that offers both pleasing aesthetics and high strength [14]. In this multilayer technology, the upper half of the manufacturing disc, which represents the incisal area of the restoration, is made of translucent zirconia material with a high yttria content. The lower half, which represents the cervical area, is made of low translucent zirconia with 3 mol% yttria content; thus, the mechanical properties of these materials are expected to be different by layer [7, 14]. Therefore, dental technicians need to have enough knowledge and carefully handle those translucent multilayered zirconia materials during the fabrication process using a computer-aided design/manufacturing (CAD/CAM) system.

There are a variety of translucent multilayered zirconia materials made with different multilayer technologies in the dental market, and more research is required to evaluate the effect of those technologies on the flexural strength of the zirconia material. Therefore, the present study evaluated the flexural strength of two translucent multilayered zirconia materials produced with different multilayer technologies. The null hypotheses tested were that there is no difference in flexural strength values of two translucent zirconia materials produced with different multilayer technologies and that there is no difference in flexural strength values of the individual layers of those two multilayered materials.

2. Methodology

2.1. Sample and Materials

Eighty bar-shaped zirconia specimens were prepared from two different partially sintered multilayered zirconia discs and divided into eight groups (n = 10) based on the multilayered zirconia materials used and the individual layers of the discs (Figure 1): Dentin Prime, Transition Prime, Translucent Prime, Multilayered Prime, Dentin HTML, Transition HTML, Translucent HTML, and Multilayered HTML. The bar-shaped zirconia specimens were cut to include all the layers from translucent to dentin in the Multilayered Prime and Multilayered HTML groups.

Two types of translucent multilayered zirconia materials produced with two different multilayer technologies were used in this study (Table 1): IPS e.max® ZirCAD Prime (Ivoclar, USA) and KATANA™ Multilayered Zirconia HTML (Kuraray Noritake Dental, EU). The ZirCAD Prime disc measures 16 mm in height with a 98.5 mm diameter and comprises three layers with different yttria contents based on the manufacturer data: The incisal (translucent) layer represents 18% of the total disc height, the transition layer represents 25% of the disc height, and the dentin (body) layer represents 57% of the disc height (Figure 1). The Multilayered Zirconia HTML disc measures 18 mm in height with a 98.5 mm diameter and comprises four layers of zirconia with a gradient shade technology: The enamel (translucent) layer represents 35% of the disc height, two transition layers represent 30%, and the dentin layer represents 35% (Figure 1).

The zirconia specimens were prepared by one individual based on the European standard ISO 6872:2015 using an automatic precision cutting machine (Struers Secotom-60, Struers, USA). The diamond saw was used to cut the specimens into rectangular-shaped bars directly from the zirconia discs. The zirconia specimens were then finished using a grinder/polisher machine (Minimet, Buehler, Lake Bluff, IL, USA) with 600-grit paper until they reached the standard dimensions of 1.2 ± 0.2 mm thickness by 4.0 ± 0.2 mm width and 15.0 ± 0.2 mm length. Subsequently, they were polished with 1200 and 2400-grit paper.

2.2. Sintering Procedures and Flexural Strength Test

The zirconia specimens were sintered using a calibrated ZirkonZahn dental ceramic furnace (ZirkonZahn; Zirkonofen 700 Vakuum, Zirkonzahn GmbH, Gais, Austria) directly after cutting from each layer of the multilayered zirconia discs. The sintering conditions were based on the standard sintering programs following the manufacturer’s instructions (Table 2). Before the bending test, the specimens were cleaned for 10 min using ultrasonic cleaning in distilled water.

A static three-point bending test based on ISO 6872 was performed using a universal testing machine (Zwick/Roell type: Xforce HP) to determine the flexural strength of each layer of the multilayered zirconia discs. Each zirconia specimen was placed on two supporting beams measuring 1.5–5 ± 0.2 mm in diameter. The zirconia specimens were loaded using the universal testing machine centrally at a crosshead speed of 1 mm/min until fracture occurred. The span was set at 13.0 mm. Specimens were tested dry at room temperature. The load at fracture was recorded in N and the flexural strengths were calculated in MPa automatically as recommended in the standard and based on the following formula:where σ is the flexural strength (MPa), N is the fracture load (in Newton), l is the distance between the supports (in mm), b is the width of the specimen (in mm), and d is the thickness of the specimen (in mm).

2.3. Statistical Analysis

The normal distribution and homogeneity of the data were verified by the Kolmogorov–Smirnov test and Levene test. Then, the differences in the flexural strength among the tested groups were analyzed using a two-way analysis of variance (ANOVA), followed by Tukey’s post hoc test (IBM SPSS Statistics 22; SPSS Inc., Chicago, IL, USA). Results are considered statistically significant at . The power analysis was based on previous research with a comparable study design to detect differences between zirconia-based specimens [14, 15].

3. Results

The three-point flexural strength data and significance levels of all groups are shown in Figure 2. There were significant differences in flexural strength values among the groups according to the two multilayered zirconia materials with different multilayer technologies used in the study (). Generally, the specimens made of HTML zirconia material had significantly () higher flexural strength than those made of IPS e.max® ZirCAD Prime material but were not significantly different () compared to the Dentin Prime group.

Figure 3 compares the flexural strength of the two multilayered zirconia materials with different multilayer technologies regardless of the individual layers. The Dentin Prime specimens had significantly () highest flexural strength (743 ± 116 MPa) compared to those in Translucent Prime (514 ± 120 MPa), Transition Prime (575 ± 102 MPa), and Multilayered Prime (531 ± 132 MPa) groups. Conversely, the specimens from the individual layers of HTML zirconia material were not significantly different () in flexural strength from the Dentin HTML (763 ± 56 MPa), Translucent HTML (791 ± 106 MPa), Transition HTML (816 ± 85 MPa), and Multilayered HTML (793 ± 102 MPa) groups.

4. Discussion

The study results indicated that the multilayered zirconia material with different yttria contents by layer significantly differed in flexural strength values compared to the multilayered zirconia material with gradient shade technology; hence, the first null hypothesis was rejected. However, the study showed no significant differences in the flexural strength of individual layers of the multilayered zirconia material with gradient shade technology compared to individual layers of the other material with varying yttria contents. Therefore, the second null hypothesis, assuming that there is no difference in the flexural strength values of the individual layers of the two multilayered zirconia materials tested in this study, was partially rejected.

Even though newly developed multilayered zirconia materials are more translucent than traditional zirconia materials stabilized with 3% mol yttria [4, 7–9], the balance between strength and translucency properties is a significant factor for the success of those materials. Manufacturers have implemented different technologies for enhancing the material translucency to mimic the optical properties of natural teeth. This study evaluated the flexural strength of two multilayered zirconia materials made with different technologies. The IPS e.max® ZirCAD Prime is a multilayered material with two zirconia materials stabilized with different yttria contents (3% and 5% mol) in one disc, each material in one layer with an intermediate transition layer containing a mix of the two between them to facilitate a gradual change in the chemical composition. Conversely, KATANA™ Multilayered Zirconia HTML consists of only translucent zirconia material stabilized with 5% mol yttria in each layer but with varying color additives to control the translucency. Regardless of the implemented technology, the preferable technology is the one that better balances the strength and translucency properties.

The present study revealed statistically significant differences in the flexural strength of the individual layers of the ZirCAD Prime disc, with the dentin layer having the highest flexural strength. This result can be explained by the fact that the dentin layer consists of the traditional zirconia material stabilized with 3% mol yttria which has a high strength and tough metastable tetragonal crystal phase due to transformation toughness [1, 5, 6]. In this mechanism, surface stresses at the tips of preexisting cracks encountered during fabrication induce the transformation of tetragonal crystals into monoclinic crystals, thereby increasing the volume and compressing the surface to inhibit further crack propagation and increase the strength and toughness properties [5, 6]. In contrast, the translucent layer of the ZirCAD Prime material had the lowest flexural strength values compared to the other layers. This layer consists of highly translucent zirconia material stabilized with a higher yttria content (5 mol%) compared to traditional zirconia. The increase in yttria content results in more cubic phase formation at the expense of the metastable tetragonal phase at the microstructural level [7, 8, 16, 17]. As previously reported, the latter influences the ability for transformation toughening of those cubic containing zirconia materials [16, 17]. Therefore, the strength and toughness properties of the translucent layer might be negatively influenced by using a higher yttria content compared to the dentin layer. Moreover, the flexural strength of the transition layer of the ZirCAD Prime material was higher but not significantly different from the translucent layer. The higher strength properties of this layer compared to the translucent layer might be achieved by the presence of the tough zirconia material with 3 mol% yttria.

The other multilayered zirconia material (KATANA HTML) tested was not statistically significantly different in mean flexural strength among the individual layers, indicating that there are few differences in the mechanical properties throughout the different layers. This may be attributed to the similar yttria content used in each layer of this multilayered zirconia material, and the translucency properties differed only by the amount of color additives. These results are in line with previous studies that reported no significant differences in the flexural characteristics of zirconia materials subjected to different coloring procedures [18, 19]. Conversely, a previous study reported that more color additives with different amounts of iron and titanium in the dentin layer resulted in an increased monoclinic content after low-temperature degradation [20]. The high monoclinic content has a deteriorating effect on the mechanical properties and results in an unstable material that experiences crack development under severe conditions. In this study, the flexural strength of the dentin layer of the KATANA HTML material was lower but not statistically different compared to other layers. Further investigations are needed to understand the low-temperature degradation behavior of the individual layers of multilayered zirconia materials made with gradient shade technology.

For fabricating monolithic ceramic restorations, silicates and zirconia are two commonly used materials in dentistry [10, 21, 22]. Vichi et al. [23] conducted a study on the flexural strength values of silicates and found that their strength values ranged from 127.65 to 350.88 MPa. These materials are suitable only for single-unit prostheses and for 3-unit prostheses not involving molar restoration, as they meet the flexural strength values required for classes 1, 2, and 3 of ISO standard 6872:2015 [24]. Compared to the findings of this study on zirconia materials, it was observed that multilayered zirconia materials for monolithic restorations showed higher strength values than silicates. All of the multilayered zirconia materials tested in this study achieved flexural strength values higher than 200 MPa of what is required for classes 1, 2, and 3 of ISO standard 6872:2015. Additionally, zirconia materials with a gradient shade technology demonstrated even higher flexural strength values, making them suitable for clinical indications of 3-unit prostheses that involve molar restoration, based on class 4 of the ISO standard 6872:2015 [24].

In dental laboratories, the tested multilayered zirconia materials are milled from presintered discs to fabricate FDPs using CAD/CAM technology [25]. This technology allows the dental technician to place the intended prosthesis within the multilayered zirconia disc by moving it up and down using the CAM software. This study clarified the significant effect of different yttria contents on the flexural strength of the individual layers of the multilayered ZirCAD Prime material compared to the KATANA HTML material with similar yttria contents in each layer. Although the ZirCad Prime offers high aesthetical outcomes with varying translucency for each layer, it might be more sensitive to the placement procedures of dental prostheses in the disc than the KATANA HTML material with a gradient shade technology. Those procedures, therefore, critically influence the clinical success of dental prostheses, especially if the weak parts of the prosthesis, such as the connectors, are placed in transition or translucent layers [13, 26–28]. Further studies are needed to evaluate the influence of these placement procedures on prostheses made of multilayered zirconia materials with different yttria contents.

One of the limitations of laboratory studies evaluating multilayered zirconia materials is the challenge of standardizing the preparation of the test specimens made of the different layers. The position of the specimens prepared from each layer of the presintered disc may have differed, which could contribute to significant differences that affect the study results. Choosing the appropriate standard for conducting the test is crucial for meeting the study’s aims. Additionally, comparing test results with other studies using the same test protocols is important. In this study, all specimens were prepared following the ISO 6872:2015 before sintering.

The laboratory study that evaluates dental restorative materials is recommended to be clinically relevant to mimic the clinical failures of dental restorations [13, 27, 29]. The specimen shape might be one of the limitations of this study. Although the specimen dimensions are based on ISO standards, the strength and fracture behavior of the different multilayered translucent zirconia materials tested should be further investigated with anatomically shaped specimens, such as crowns and bridges. Moreover, other material properties should be investigated such as elemental composition, grain sizes, microhardness, and fracture toughness of the individual layers of translucent zirconia materials made with different multilayer technologies.

5. Conclusion

Within the limitations of the study, the following can be concluded: Translucent zirconia materials produced with different multilayer technologies are relatively different from each other regarding their chemical composition. Multilayered zirconia materials produced with different yttria contents by layer have lower flexural strength than those produced with a gradient shade technology and the same yttria content for each layer. Therefore, various factors such as the type of prostheses, nesting strategies of prostheses within the zirconia disc, and the desired aesthetical requirements should be considered when selecting the multilayered zirconia materials.

Data Availability

The data that support the findings of this study are available from the corresponding author upon reasonable request.

Conflicts of Interest

The author reports no conflicts of interest in this work.

Acknowledgments

The author would like to thank Ivoclar Vivadent AB for providing study materials.

References

I. Denry and J. R. Kelly, “State of the art of zirconia for dental applications,” Dental Materials, vol. 24, no. 3, pp. 299–307, 2008.
View at: Publisher Site | Google Scholar
T. Miyazaki, T. Nakamura, H. Matsumura, S. Ban, and T. Kobayashi, “Current status of zirconia restoration,” Journal of Prosthodontic Research, vol. 57, no. 4, pp. 236–261, 2013.
View at: Publisher Site | Google Scholar
I. Sailer, M. Strasding, N. A. Valente, M. Zwahlen, S. Liu, and B. E. Pjetursson, “A systematic review of the survival and complication rates of zirconia-ceramic and metal-ceramic multiple-unit fixed dental prostheses,” Clinical Oral Implants Research, vol. 29, no. S16, pp. 184–198, 2018.
View at: Publisher Site | Google Scholar
R. Shahmiri, O. C. Standard, J. N. Hart, and C. C. Sorrell, “Optical properties of zirconia ceramics for esthetic dental restorations: a systematic review,” The Journal of Prosthetic Dentistry, vol. 119, no. 1, pp. 36–46, 2018.
View at: Publisher Site | Google Scholar
R. H. J. Hannink, P. M. Kelly, and B. C. Muddle, “Transformation toughening in irconia-containing ceramics,” Journal of the American Ceramic Society, vol. 83, no. 3, pp. 461–487, 2000.
View at: Google Scholar
A. G. Evans and A. H. Heuer, “Transformation toughening in ceramics: martensitic transfo mations in crack-tip stress fields,” Journal of the American Ceramic Society, vol. 63, no. 5-6, pp. 241–248, 1980.
View at: Google Scholar
A. Elsayed, G. Meyer, S. Wille, and M. Kern, “Influence of the yttrium content on the fracture strength of monolithic zirconia crowns after artificial aging,” Quintessence International, vol. 50, no. 5, pp. 344–348, 2019.
View at: Publisher Site | Google Scholar
F. Zhang, M. Inokoshi, M. Batuk et al., “Strength, toughness and aging stability of highly-translucent Y-TZP ceramics for dental restorations,” Dental Materials, vol. 32, no. 12, pp. e327–e337, 2016.
View at: Publisher Site | Google Scholar
A. R. Reyes, J. B. Dennison, J. M. Powers, M. Sierraalta, and P. Yaman, “Translucency and flexural strength of translucent zirconia ceramics,” The Journal of Prosthetic Dentistry, vol. 129, no. 4, pp. 644–649, 2023.
View at: Publisher Site | Google Scholar
A. F. de Mendonca, M. Shahmoradi, C. V. D. Gouvea, and A. Ellakwa, “Microstructural and mechanical characterization of CAD/CAM materials for monolithic dental restorations,” Journal of Prosthodontics, vol. 28, no. 2, pp. 587–594, 2018.
View at: Google Scholar
A. Worni, J. Katsoulis, L. Kolgeci, M. Worni, and R. Mericske-Stern, “Monolithic zirconia reconstructions supported by teeth and implants: 1–3-year results of a case series,” Quintessence International, vol. 48, no. 6, pp. 459–467, 2017.
View at: Publisher Site | Google Scholar
M. Michailova, A. Elsayed, G. Fabel, D. Edelhoff, I. M. Zylla, and B. Stawarczyk, “Comparison between novel strength-gradient and color-gradient multilayered zirconia using conventional and high-speed sintering,” Journal of the Mechanical Behavior of Biomedical Materials, vol. 111, Article ID 103977, 2020.
View at: Publisher Site | Google Scholar
N. Heidari, R. Amawi, P. Seweryniak, F. Bakitian, and P. V. von Steyern, “Fracture resistance and fracture behaviour of monolithic multi-layered translucent zirconia fixed dental prostheses with different placing strategies of connector: an in vitro study, clinical,” Cosmetic and Investigational Dentistry, vol. 14, pp. 61–69, 2022.
View at: Publisher Site | Google Scholar
T. Strasser, M. Wertz, A. Koenig, T. Koetzsch, and M. Rosentritt, “Microstructure, composition, and flexural strength of different layers within zirconia materials with strength gradient,” Dental Materials, vol. 39, no. 5, pp. 463–468, 2023.
View at: Google Scholar
W. Frąckiewicz, M. Królikowski, K. Kwiatkowski, E. Sobolewska, P. Szymlet, and M. Tomasik, “Comparison of dental zirconium oxide ceramicsproduced using additive and removal technology for prosthodontics and restorative dentistry-strength and surface tests: an in vitro study,” Materials, vol. 17, no. 1, p. 168, 2024.
View at: Publisher Site | Google Scholar
Y. Zhang and B. R. Lawn, “Novel zirconia materials in dentistry,” Journal of Dental Research, vol. 97, no. 2, pp. 140–147, 2018.
View at: Google Scholar
C. D. Holman, W. Lien, F. F. Gallardo, and K. S. Vandewalle, “Assessing flexural strength degradation of new cubic containing zirconia materials,” The Journal of Contemporary Dental Practice, vol. 21, no. 2, pp. 114–118, 2020.
View at: Google Scholar
M. Sedda, A. Vichi, M. Carrabba, A. Capperucci, C. Louca, and M. Ferrari, “Influence of coloring procedure on flexural resistance of zirconia blocks,” The Journal of Prosthetic Dentistry, vol. 114, no. 1, pp. 98–102, 2015.
View at: Publisher Site | Google Scholar
N. K. Yu and M. G. Park, “Effect of different coloring liquids on the flexural strength of multilayered zirconia,” The Journal of Advanced, vol. 11, no. 4, pp. 209–214, 2019.
View at: Google Scholar
S. Wille, P. Zumstrull, V. Kaidas, L. K. Jessen, and M. Kern, “Low temperature degradation of single layers of multilayered zirconia in comparison to conventional unshaded zirconia: phase transformation and flexural strength,” Journal of the Mechanical Behavior of Biomedical Materials, vol. 77, pp. 171–175, 2018.
View at: Google Scholar
F. Huettig and U. P. Gehrke, “Early complications and performance of 327 heat-pressed lithium disilicate crowns up to five years,” The Journal of Advanced Prosthodontics, vol. 8, no. 3, pp. 194–200, 2016.
View at: Publisher Site | Google Scholar
C. I. M. B. Leitão, G. V. O. Fernandes, L. P. P. Azevedo, F. M. Araújo, H. Donato, and A. R. M. Correia, “Clinical performance of monolithic CAD/CAM tooth-supported zirconia restorations: systematic review and meta-analysis,” Journal of Prosthodontic Research, vol. 66, no. 3, pp. 374–384, 2022.
View at: Publisher Site | Google Scholar
A. Vichi, Z. Zhao, G. Paolone et al., “Factory crystallized silicates for monolithic metal-free restorations: a flexural strength and translucency comparison test,” Materials, vol. 15, no. 21, Article ID 7834, 2022.
View at: Publisher Site | Google Scholar
ISO 6872:2015, “Dentistry—ceramic materials,” Geneva, Switzerland, 2015, International Organization for Standardization.
View at: Google Scholar
T. Miyazaki, Y. Hotta, J. Kunii, S. Kuriyama, and Y. Tamaki, “A review of dental CAD/CAM: current status and future perspectives from 20 years of experience,” Dental Materials, vol. 28, no. 1, pp. 44–56, 2009.
View at: Google Scholar
K. Plengsombut, J. D. Brewer, E. A. Monaco, and E. L. Davis, “Effect of two connector designs on the fracture resistance of all-ceramic core materials for fixed dental,” The Journal of Prosthetic Dentistry, vol. 101, no. 3, pp. 166–173, 2009.
View at: Publisher Site | Google Scholar
F. Bakitian, P. Seweryniak, E. Papia, C. Larsson, and P. Vult von Steyern, “Load-bearing capacity of monolithic zirconia fixed dental prostheses fabricated with different connector designs and embrasure shaping methods,” Journal of Prosthodontics, vol. 28, no. 1, pp. 64–70, 2019.
View at: Publisher Site | Google Scholar
C. Subsomboon and S. Urapepon, “Effect of connector configuration on the fracture load in conventional and translucent zirconia three-unit fixed dental prostheses,” The Journal of Advanced Prosthodontics, vol. 15, no. 4, pp. 171–178, 2023.
View at: Google Scholar
K. J. Anusavice, K. Kakar, and N. Ferree, “Which mechanical and physical testing methods are relevant for predicting the clinical performance of ceramic-based dental prostheses?” Clinical Oral Implants, vol. 18, no. 3, pp. 218–231, 2007.
View at: Google Scholar

Copyright

Copyright © 2024 Fahad Bakitian. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

161

Downloads

104

Citations