How Water Content Can Influence the Chemomechanical Properties and Physical Degradation under Aging of Experimental Adhesives

Table 1

Mean ± standard deviation and results of Tukey’s test of degree of conversion, flexural strength, modulus of elasticity, and compressive strength of adhesives.

	Degree of conversion (%)	Flexural strength (MPa)	Modulus of elasticity (GPa)	Compressive strength (MPa)
0 wt%	68.09 ± 0.14 A	109.4 ± 20.5 A	2.7 ± 0.2 A	141.4 ± 19.5 A
10 wt%	87.07 ± 0.81 B	141.6 ± 6.71 B	2.7 ± 0.4 A	151.2 ± 27.8 A
16 wt%	89.87 ± 0.24 B	107.8 ± 15.8 A	2.2 ± 0.3 B	98.8 ± 18.0 B

Different letters represent statistically significant differences (). Uppercase letters refer to columns.